Abstract:In recent years, a new kind of abnormal fracture phenomena of composite insulator occurred in high voltage transmission lines in several countries, which was totally different from brittle fracture and normal fracture. According to the general characteristic features of the fracture, this type of failure was named decay-like fracture of composite insulator by the author. In this paper, a decay-like fractured composite insulator was investigated and microscopic physic-chemical properties of decay-like fractured Fiber Reinforced Plastic (FRP) core rod were analyzed. Scanning Electron Microscope (SEM), Thermal Gravimetric Analysis (TGA) and Fourier Transform Infrared (FTIR) Spectroscopy methods were employed to explain the microscopic morphology characteristics and chemical component changes of decay-like fractured composite insulator, and to further explain the reasons for the name of decay-like fracture in terms of "crisp" and "decay-like". The main microscopic feature of decay-like fracture is the degradation and deterioration of the epoxy resin matrix in FRP rod. The mechanism of decay-like fracture of composite insulator could be summarized as follows. Due to the liquids penetration into the sheath-core interface, hydrolysis of silane coupling agent with bad quality leads to poor adhesion strength and interface voids, which results in distortion of electric field at the sheath-core interface. Under the combined action of damp condition and high electric field, discharge and current appear along the FRP rod surface. Epoxy resin matrix is eroded in the presence of discharge and current, and then is soften, melt, evaporated. Meanwhile, ion-exchange and hydrolysis process happen between glass fibers under the combined action of mechanical stress and nitric acid produced by discharge in the presence of moisture. Fiber-resin interface in FRP rod is separated owing to the erosion of epoxy resin. The degradation direction of the decay-like fracture is from outside to inside of FRP rod, and the interface between silicone rubber sheath and FRP rod is confirmed to be the initial deterioration area of the decay-like fracture. The criterion to distinguish the differences between the decay-like fracture, brittle fracture and normal fracture depends on whether the epoxy resin matrix is degraded and deteriorated or not.

Study on the Degradation of FRP Rod of Composite Insulator under Electrical Stress and Salt Fog

Degradation Characteristics of Epoxy Resin of GFRP Rod in the Decay-Like Fracture of Composite Insulator

Decay-like Fracture Mechanism of Silicone Rubber Composite Insulator

Study on the Mechanism Effect of Bending Loads on the Decay-like Degradation of Composite Insulator GFRP Core Rod

Composite Insulator Interface Discharge Accelerated Decay-Like Aging and Analysis

Influence of Surface Discharge on Resin Degradation in Decay-like Fracture of Composite Insulators.

Study on Decay-Like Fracture of Composite Insulator, Part II:Experimental Simulation and Preventive Method Discussion of Decay-Like Fracture

Effect of Electrical Stress on Glass Fiber Reinforced Polymer Used in High Voltage Composite Insulator under Wet Environment

Study on Decay-Like Fracture of Composite Insulator：Part I- the Principal Character, Definition and Criterion of Decay-Like Fracture

Effects of Corona Discharge on the Properties of Fiber Reinforced Plastics Used in Composite Insulator

Effect of acid corrosion on properties of composite insulator core rod

Failure analysis of decay-like fracture of composite insulator

Characterization of material degradation mechanism of carbon fiber reinforced epoxy resin composites under ultraviolet radiation and salt‐fog synergistic environment

Failure Analysis of a Field Brittle Fracture Composite Insulator: Characterization by FTIR Analysis and Fractography

Fiber and interface failure characterization of glass fiber reinforced polymer for composite insulators after liquid permeation

Study on the Morphology Characteristics of Epoxy Resin of Composite Insulator under Acid-heat Condition

Surface Micro-Crack Initiated Brittle Fracture in Fiber Reinforced Plastic Rod of Composite Insulator

RESEARCH ON BRITTLE FRACTURE OF FRP RODS AND THE TEST METHOD

The Aging Behavior and Life Prediction of CFRP Rods under a Hygrothermal Environment

Effect of seawater and stress coupling on the durability of carbon fibre-reinforced polymer

Research on the brittle fracture of FRP rod and its test method