Abstract:In recent years, a new kind of abnormal fracture phenomena of composite insulator occurred in high voltage transmission lines in several countries, which was totally different from brittle fracture and normal fracture. According to the general characteristic features of the fracture, this type of failure was named decay-like fracture of composite insulator by the author. In this paper, a decay-like fractured composite insulator was investigated and microscopic physic-chemical properties of decay-like fractured Fiber Reinforced Plastic (FRP) core rod were analyzed. Scanning Electron Microscope (SEM), Thermal Gravimetric Analysis (TGA) and Fourier Transform Infrared (FTIR) Spectroscopy methods were employed to explain the microscopic morphology characteristics and chemical component changes of decay-like fractured composite insulator, and to further explain the reasons for the name of decay-like fracture in terms of "crisp" and "decay-like". The main microscopic feature of decay-like fracture is the degradation and deterioration of the epoxy resin matrix in FRP rod. The mechanism of decay-like fracture of composite insulator could be summarized as follows. Due to the liquids penetration into the sheath-core interface, hydrolysis of silane coupling agent with bad quality leads to poor adhesion strength and interface voids, which results in distortion of electric field at the sheath-core interface. Under the combined action of damp condition and high electric field, discharge and current appear along the FRP rod surface. Epoxy resin matrix is eroded in the presence of discharge and current, and then is soften, melt, evaporated. Meanwhile, ion-exchange and hydrolysis process happen between glass fibers under the combined action of mechanical stress and nitric acid produced by discharge in the presence of moisture. Fiber-resin interface in FRP rod is separated owing to the erosion of epoxy resin. The degradation direction of the decay-like fracture is from outside to inside of FRP rod, and the interface between silicone rubber sheath and FRP rod is confirmed to be the initial deterioration area of the decay-like fracture. The criterion to distinguish the differences between the decay-like fracture, brittle fracture and normal fracture depends on whether the epoxy resin matrix is degraded and deteriorated or not.

Failure Analysis of a Field Brittle Fracture Composite Insulator: Characterization by FTIR Analysis and Fractography

Failure Analysis of a Field Brittle Fracture Composite Insulator: Characterisation by X-ray Photoelectron Spectroscopy Analysis

Analysis of the Acid Sources of a Field Brittle Fractured Composite Insulator

Brittle Fracture of High Voltage Composite Insulators

Surface Micro-Crack Initiated Brittle Fracture in Fiber Reinforced Plastic Rod of Composite Insulator

Micro Failure Analysis of Fiber Metal Laminates

ULTRASONIC DETECION ON CRACK OF FRP ROD IN BRITTLE FRACTURE OF COMPOSITE INSULATOR

Failure analysis of decay-like fracture of composite insulator

Analysis of a Fractured 500 Kv Composite Insulator - Identification of Aging Mechanisms and Their Causes

Decay-like Fracture Mechanism of Silicone Rubber Composite Insulator

Fracture Fault Analysis and Aging Mechanism Study for 500 kV Composite Insulator

RESEARCH ON BRITTLE FRACTURE OF FRP RODS AND THE TEST METHOD

Study on Decay-Like Fracture of Composite Insulator：Part I- the Principal Character, Definition and Criterion of Decay-Like Fracture

Research on the Brittle Fracture of FRP Rods and Its Acoustic Emission Detection

Fiber and interface failure characterization of glass fiber reinforced polymer for composite insulators after liquid permeation

Degradation Characteristics of Epoxy Resin of GFRP Rod in the Decay-Like Fracture of Composite Insulator

Research on the brittle fracture of FRP rod and its test method

Influence of Surface Discharge on Resin Degradation in Decay-like Fracture of Composite Insulators.

Study on the Degradation of FRP Rod of Composite Insulator under Electrical Stress and Salt Fog

Influence of Diffusion of Nitric Acid to Brittle Fracture of Composite Insulators

Study on Decay-Like Fracture of Composite Insulator, Part II:Experimental Simulation and Preventive Method Discussion of Decay-Like Fracture