Abstract:This study investigated defect formation and strain distribution in high-Mg-content Al-Mg alloys during normal rolling and cross-rolling processes. The finite element analysis (FEA) revealed the presence of wave defects and strain localization-induced zipper cracks in normal cold rolling, which were confirmed by the experimental results. The concentration of shear strain played a significant role in crack formation and propagation. However, the influence of wave defects was minimal in the cross-rolling process, which exhibited a relatively uniform strain distribution. Nonetheless, strain concentration at the edge and center regions led to the formation of zipper cracks and edge cracks, with more pronounced propagation observed in the experiments compared to FEA predictions. Furthermore, texture evolution was found to be a crucial factor affecting crack propagation, particularly with the development of the Goss texture component, which was observed via electron backscattered diffraction analysis at bending points. The Goss texture hindered crack propagation, while the Brass texture allowed cracks to pass through. This phenomenon was consistent with both FEA and experimental observations. To mitigate edge crack formation and propagation, potential strategies involve promoting the formation of the Goss texture at the edge through alloy and process conditions, as well as implementing intermediate annealing to alleviate stress accumulation. These measures can enhance the overall quality and reliability of Al-Mg alloys during cross-rolling processes. In summary, understanding the mechanisms of defect formation and strain distribution in Al-Mg alloys during rolling processes is crucial for optimizing their mechanical properties. The findings of this study provide insights into the challenges associated with wave defects, strain localization, and crack propagation. Future research and optimization efforts should focus on implementing strategies to minimize defects and improve the overall quality of Al-Mg alloys in industrial applications.

Prediction of edge cracks and plastic-damage analysis of Mg alloy sheet in rolling

A continuum damage model for Mg/Al composite sheets rolling: Theoretical development and application

Prediction of magnesium alloy edge crack in edge-constraint rolling process by using a modified GTN model

Microstructural analysis of edge cracking in magnesium alloy sheet under rolling

Edge Cracks and Temperature Field of AZ31B Magnesium Alloy Sheet

Predicted Edge Crack Model of Hot Rolling for AZ31 Magnesium Alloy

Effect of Temperature Field and Stress Field of Different Crack Behavior on Twins and Dislocations under Mg Alloy Rolling

Unveiling the Underlying Mechanism of Forming Edge Cracks Upon High Strain-Rate Rolling of Magnesium Alloy

Simulation and confirmatory experiment on rolling of magnesium alloy sheets with temperature gradient

Comparison of edge crack behavior of Mg sheets prepared by online heating rolling

Numerical simulation of effect of temperature gradient on rolling of magnesium alloy sheets

Study on Rolling Defects of Al-Mg Alloys with High Mg Content in Normal Rolling and Cross-Rolling Processes

Effect of variable thickness cross rolling on edge crack and microstructure gradient of AZ31 magnesium alloy

The Edge Crack, Texture Evolution, and Mechanical Properties of Mg-1Al-1Sn-Mn Alloy Sheets Prepared Using On-Line Heating Rolling

Failure prediction of magnesium alloys based on improved CDM model

DEFORMATION ANALYSIS OF THE HOT ROLLING PROCESS OF ALUMINUM ALLOY

The Effect of Texture on the Very High Cycle Fatigue Performance and Deformation Mechanism of Rolled AZ31B Magnesium Alloys

Forming Limit Analysis of Mg-2Zn-1.2Al-0.2Ca-0.2RE Alloy Sheet Using Ductile Fracture Models

Initiation and Suppression of Crack Propagation during Magnesium Alloy Rolling

Deformation Microstructure and Characteristics of Cast-Rolling and Normal Rolling AZ31 Magnesium Alloy Sheets

Effect of Rolling Reduction on the Microstructure and Mechanical Properties of Hot-Rolled Mg-Li-Al-Ca Alloys