Abstract:Magnesium sheet metal alloys have a hexagonal close packed (hcp) crystal structure that leads to severe evolving anisotropy and tension-compression asymmetry as a result of the activation of different deformation mechanisms (slip and twinning) that are extremely challenging to model numerically. The low density of magnesium alloys and their high specific strength relative to steel and aluminum alloys make them promising candidates for automotive light-weighting but standard phenomenological plasticity models cannot adequately capture the complex plastic response of these materials. In this study, the constitutive plastic behavior of a rare-earth magnesium alloy sheet, ZEK100 (O-temper), was considered at room temperature, under quasi-static conditions. The CPB06 yield criterion for hcp materials was employed along with a non-associative flow rule in which the yield function and plastic potential were calibrated for a range of plastic deformation levels to account for evolving anisotropy under proportional loading. The non-associative flow rule has not previously been applied to magnesium alloys which require the use of flexible constitutive models to capture the severe anisotropy and its evolution with plastic deformation. The non-associative flow rule can provide the required flexibility by decoupling the yield function and plastic potential. For the associative flow rule, such flexibility can only be achieved by multiple linear transformations of the stress tensor resulting in expensive models for calibration and simulations. The constitutive model was implemented as a user material subroutine (UMAT) within the commercial finite element software, LS-DYNA, for general 3-D stress states along with an interpolation technique to consider the evolution of anisotropy based upon the plastic work. To evaluate the accuracy of the implemented model, predictions of a single-element model were compared with the experimental results in terms of flow stresses and plastic flow directions under various proportional loading conditions and along different test directions. Finally, to assess the predictive capabilities of the model, full-scale simulations of coupon-level formability experiments were performed and compared with experimental results in terms of far-field load-displacement and local strain paths. Using these experiments, the constitutive model was evaluated across the full range of representative stress states for sheet metal forming operations. It was shown that the predictions of the model were in very good agreement with experimental data.

Failure prediction of magnesium alloys based on improved CDM model

Prediction of the Ultra-Low-Cycle Fatigue Damage of Q345qC Steel and Its Weld Joint

Study on the Prediction Method of the Ultra-Low-Cycle Fatigue Damage of Steel

Enhanced CDM model accounting of stress triaxiality and Lode angle for ductile damage prediction in metal forming

Continuum Damage Mechanics Based Fatigue Life Prediction and Fatigue Property Analysis of Pitting Corrosion Steel Bars

Material Model Development of Magnesium Alloy and Its Strength Evaluation

A continuum damage model for Mg/Al composite sheets rolling: Theoretical development and application

A mesoscopic damage model for the low-cycle fatigue of an extruded magnesium alloy

Application of an Evolving Non-Associative Anisotropic-Asymmetric Plasticity Model for a Rare-Earth Magnesium Alloy

A New Constitutive Model for Thermal Deformation of Magnesium Alloys

Broad Stress Triaxiality Ratio Band Fracture Experiments in DP900 Metal Sheets and Corresponding Predictive Capability of Advanced Phenomenological and Micromechanical Fully Coupled Damage Models

A coupled ductile damage model for metal matrix composites: Development and application

Forming Limit Analysis of Mg-2Zn-1.2Al-0.2Ca-0.2RE Alloy Sheet Using Ductile Fracture Models

Forming Limit Prediction of Anisotropic Aluminum Magnesium Alloy Sheet AA5052-H32 Using Micromechanical Damage Model

Modelling of dynamic behaviour of orthotropic metals including damage and failure

Predicting Plastic Behavior of Magnesium Alloy Tube Bending with Comprehensive Constitutive Models

Simulation of Magnesium Alloy AZ31 Sheet During Cylindrical Cup Drawing with Rate Independent Crystal Plasticity Finite Element Method

A Thermal Damage-Coupled Constitutive Model for Predicting Fracture and Microstructure Evolution and Its Application in the Hot Spinnability Process

Investigation on the inhomogeneous deformation of magnesium alloy during bending using an advanced plasticity model

Prediction of High Cycle Fatigue Strength for Additive Manufactured Metals by Defects Incorporated Crystal Plasticity Modeling

A novel damage mechanics and XGBoost based approach for HCF life prediction of cast magnesium alloy considering internal defect characteristics