Abstract:In our previous work, we designed a new as-cast Mg–Y–Zn–Al–Li alloy with a high elastic modulus of 52.9 GPa. The alloy was further subjected to hot deformation under different rolling reductions (40% and 80%) in this work. The microstructure evolution, texture and mechanical properties of Mg–Y–Zn–Al–Li alloy compared with Mg–Y–Zn alloy were systematically investigated. The result showed that the Mg–Y–Zn–Al–Li alloy with a rolling reduction of 40% displayed a more homogeneous fine microstructure and a weakened basal texture, accompanied by the formation of Al–Li and nano-precipitates Al0.9Li34.3Mg64.5Zn0.3 phase. Compared with the Mg–Y–Zn alloy, the strength and ductility of the alloy also were obviously enhanced while possessing a weak mechanical anisotropy. Grain refinement and second phase strengthening (fine Al–Li phase and nano-precipitates Al0.9Li34.3Mg64.5Zn0.3) mainly contributed to the enhanced strength. The texture weakening, low dislocation density and non-basal slip commonly guaranteed the high ductility, especially the weakened texture gave rise to the low anisotropy. When the rolling reduction increased to 80%, the volume fraction of recrystallized grains in Mg–Y–Zn–Al–Li alloy increased significantly to73.3%. As a result, the symmetry of the texture distribution around the ND was appreciably improved. In addition, the lower dislocation density and more non-basal slip in the Mg–Y–Zn–Al–Li alloy with the rolling reduction of 80% further enhanced the ductility. Simultaneously, the anisotropic degree of mechanical was effectively minimized, which was mainly attributed to the weak symmetric texture caused by fine DRXed grains with random misorientation and non-basal pyramidal <c+a> slip.

Effect of Rolling Reduction on the Microstructure and Mechanical Properties of Hot-Rolled Mg-Li-Al-Ca Alloys

Effect of rolling temperature on microstructure and mechanical properties of hot-rolled Mg-Al-Ca-Zn-Mn alloys

Microstructure, texture and mechanical properties of the rolled high modulus Mg-Y-Zn-Al-Li alloy

Microstructure and mechanical property of multi-pass low-strain rolled Mg-Al-Zn-Mn alloy sheet

Effect of Warm Rolling on the Microstructure, Texture and Mechanical Properties of Extruded Mg–Zn–Ca–Ce/La Alloy

Effect of final rolling deformation on microstructure, work hardening and softening behavior of Mg-8Li-3Al-0.3Si alloys

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Effect of Rolling Reduction on Microstructures and Mechanical Properties of Sc-Containing Al-3.2Cu-1.5Li Alloy

Effect of rolling temperature on deformation behavior and mechanical properties of Mg-8Li-1Al-0.6Y-0.6Ce alloy

Effect of Dual Deformation Processes on the Microstructure and Mechanical Properties of Low-Alloyed Mg-Zn-Ca-Mn Alloy

Dynamic recrystallization, texture and mechanical properties of high Mg content Al–Mg alloy deformed by high strain rate rolling

Effects Of Rolling Process On Microstructure And Mechanical Property Of 7050 Aluminum Alloy

Effect of Rolling Temperature on Microstructure and Properties of Al-Mg-Li Alloy

Influence of Hot Rolling on Microstructure, Corrosion and Mechanical Properties of Mg–Zn–Mn–Ca Alloy

Microstructure Evolution and Strengthening Mechanism of Dual-Phase Mg–8.3Li–3.1Al–1.09Si Alloys during Warm Rolling

Effect of pack-rolling temperature on microstructure and mechanical properties of Mg-6Sn-3Al-1Zn Alloy

Effect of annealing treatment on the microstructure and mechanical properties of warm-rolled Mg–Zn–Gd–Ca–Mn alloys

Effect of rolling deformation on microstructure and mechanical properties of Mg–Y–Nd–Al alloy

Effect of Al addition and rolling reduction on microstructure and texture evolution of Mg–3Sn alloy during high-speed rolling

Effects of rolling processing on the microstructures, mechanical properties and strain softening behavior of biodegradable Zn-0.06 Mg alloy

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling