Abstract:An analysis of the hot flow forming of Mg-3.0 Al-1.0 Zn-0.3 Mn（AZ31 B） alloy was conducted by experiments and numerical simulations. The effects of different thickness reductions on the microstructure and mechanical properties were investigated at a temperature of 693 K, a spindle speed of 800 rev/min and a feed ratio of 0.1 mm/rev. Thickness reductions have great influence on the uniformity of microstructure along the radial direction（RD） and the grain sizes become refined and uniform when the thickness reduction reaches 45%. The c-axes of most grains are approximately parallel to the RD, with a slight inclination towards the axial direction（AD）. The best mechanical properties with UTS of 280 MPa and YS of 175 MPa near the outer surface while 266 MPa and 153 MPa near the inner surface have been achieved due to grain refinement and texture. Moreover, the material flow behavior and stress/strain distributions for singlepass reductions were studied using the ABAQUS/Explicit software. The calculated results indicate that the materials mainly suffer from triaxial compressive stresses and undergo compressive plastic strain in RD and tensile strains in other directions. The higher stress and strain rate near the outer surface lead to more refined grains than that of other regions along the RD, whereas the orientation of the maximum principal compressive stress leads to a discrepancy of the grain orientations in RD.

Edge Cracks and Temperature Field of AZ31B Magnesium Alloy Sheet

Comparison of edge crack behavior of Mg sheets prepared by online heating rolling

Deformation Microstructure and Characteristics of Cast-Rolling and Normal Rolling AZ31 Magnesium Alloy Sheets

Strain Rate and Temperature Effects on Formability and Microstructure of AZ31B Magnesium Alloy Sheet

Ameliorating the edge cracking behavior of Mg-Mn-Al alloy sheets prepared by multi-pass online heating rolling

Unveiling the Underlying Mechanism of Forming Edge Cracks Upon High Strain-Rate Rolling of Magnesium Alloy

Effects of Hot Rolling Processing on Microstructures and Mechanical Properties of Mg–3%Al–1%Zn Alloy Sheet

Effect of Final Rolling Speed on Microstructure and Performance of AZ31 Magnesium Alloy Sheet under Small Strain Condition

Grain Refinement and Orientation of AZ31B Magnesium Alloy in Hot Flow Forming under Different Thickness Reductions

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Microstructure And Mechanical Properties Of Az31 Magnesium Alloy Sheet By Hot Rolling

Thermo-Mechanical Coupled Simulation of Warm Stamping of AZ31 Magnesium Alloy Sheet

Hot Rolling of Az31 Magnesium Alloy and Its Effects on Microstructure and Mechanical Properties

Microstructure and Mechanical Properties of AZ31 Magnesium Sheet after Hot Rolling

On-line heating rolling behavior of Mg9999 sheets under large single pass reduction

Influence of Microstructure and Mechanical Properties on Formability in High Strain Rate Rolled AZ31 Magnesium Alloy Sheets

Microstructures and Mechanical Properties of Hot Rolled AZ31 Mg Alloy Sheets

Effect of rolling temperature on microstructure and mechanical properties of hot-rolled Mg-Al-Ca-Zn-Mn alloys

Grain Refining of AZ31 Magnesium Alloy During Temperature-Differential Hot Rolling

Effect of pack-rolling temperature on microstructure and mechanical properties of Mg-6Sn-3Al-1Zn Alloy

Effect of rolling reduction on microstructure, texture, mechanical properties and mechanical anisotropy of AZ31 magnesium alloys