Abstract:The present paper focuses on the heat transfer and contact pressure at the casting-die interface in squeeze casting process. Experiments were conducted and a "plate shape" was used to cast aluminum alloy A356 in H13 steel die. Based on the temperature measurements inside the die, the interfacial heat transfer coefficient (IHTC) at the metal-die interface was determined by applying an inverse approach. The pressure at the metal-die interface was measured by using Kistler pressure transducer. The acquired data were processed by a low pass filtering method based on Fast Fourier Transform (FFT). Besides, a set of methods was set up to verify the computer program for the inverse model. The results show that the pressure at the casting-die interface and the IHTC rose to the peak value almost simultaneously as soon as the pressure was applied by the press. The higher the applied pressure, the higher the peak value of the IHTC and the pressure at the casting-die interface. It was a pressure maintaining stage immediately after the pressure was applied. During this stage, the pressure at the casting-die interface decreased immediately after it reached the peak value. The IHTC sharply dropped at the beginning. Then, the decrease rate of the IHTC became lower and lower. Besides, the IHTC of the cases with pressure applied was much higher than those without pressure applied. It indicates that the applied pressure greatly improved the contact status of casting and die surfaces and reduced the thermal resistance between the two surfaces. The IHTC profiles of the cases with the pressures 23 MPa and 46 MPa applied did not make much difference, however, when the applied pressure reached 70 MPa, the influence of the pressure at the casting die interface on the IHTC became very remarkable. (C) 2017 Elsevier Ltd. All rights reserved.

Investigation on heat transfer coefficient of glass lubricated interface between P92 heat-resistant steel and H13 steel

Experimental Study on Heat Transfer Boundary Conditions for Steel Hot Extrusion Process

Heat Transfer Through Glassfiber Fabrics Coated with Silicone Resin

Boundary Parameters During Glass Lubricated Hot Extrusion of Steel Pipes

Lubrication Behavior of the Glass Lubricated Hot Extrusion Process

Glass Lubrication Technology in Steel Hot Extrusion

Experimental Investigation of High Temperature Thermal Contact Resistance with Interface Material

The effect of laminar cooling heat transfer coefficient on the temperature field of steel plate

Development of Estimation Procedure of Contact Heat Transfer Coefficient at the Part–Tool Interface in Hot Stamping Process

Experimental and modeling study of the interfacial and convective heat transfer coefficients of 6061 aluminum alloy in hot gas forming

Research methods and influencing factors of interfacial heat transfer during sub-rapid solidification process of strip casting

Investigation and Application of Inverse Determination of Interfacial Heat Transfer Coefficient in Vacuum Investment Casting

Experimental and Numerical Investigation of Forced Convection Heat Transfer of Air in Non-Sintered Porous Media

The investigation of contact ratio in mixed lubrication

Measurement of Temperature Inside Die and Estimation of Interfacial Heat Transfer Coefficient in Squeeze Casting

Analysis of Temperature and Heat Partitioning Coefficient During Friction Between Polymer and Steel

Analysis of breakthrough extrusion pressure for large scale steel pipe

Experimental Study on the Heat Transfer Behavior and Contact Pressure at the Casting-Mold Interface in Squeeze Casting of Aluminum Alloy

Investigation of oxide scale on ferritic stainless steel B445J1M and its tribological effect in hot rolling

A Study on the Heat Transfer Characteristics of Steel Plate in the Matrix Laminar Cooling Process

The Relationships Between Tribological Behaviour and Heat-Transfer Capability of Ti6Al4V Alloys