High-Performance (Ag x SbTe x /2+1.5 ) 15 (GeTe) 85 Thermoelectric Materials Prepared by Melt Spinning

Y. Chen,T. J. Zhu,S. H. Yang,S. N. Zhang,W. Miao,X. B. Zhao
DOI: https://doi.org/10.1007/s11664-010-1202-8
IF: 2.1
2010-01-01
Journal of Electronic Materials
Abstract:A new preparation process combining melt spinning and hot pressing has been developed for the (Ag x SbTe x /2+1.5 ) 15 (GeTe) 85 (TAGS-85) system. Compared with samples prepared by the traditional air-quenching and hot-pressing method, electrical conductivity and thermal conductivity are lowered. The thermoelectric performance of the TAGS-85 samples varied with changing Ag content and reached the highest ZT of 1.48 when x was 0.8 for the melt-spun sample, compared with the maximum ZT of 1.36 for the air-quenched sample. The Seebeck coefficient of the melt-spun TAGS-85 alloys was improved, while both the electrical conductivity and thermal conductivity were decreased. The net result of this process is to effectively enlarge the temperature span of ZT > 1, which will benefit industrial application.
What problem does this paper attempt to address?