Abstract:A structural change in Fe(2)SiO(4)spinel (ringwoodite) has been found by synchrotron powder diffraction study and the structure of a new high-pressure phase was determined by Monte-Carlo simulation method and Rietveld profile fitting of X-ray diffraction data up to 64 GPa at ambient temperature. A transition from the cubic spinel structure to a body centered orthorhombic phase (I-Fe2SiO4) with space group Imma and Z = 4 was observed at approximately 34 GPa. The structure of I-Fe2SiO4 has two crystallographically independent FeO6 octahedra. Iron resides in two different sites of sixfold coordination: Fe1 and Fe2, which are arranged in layers parallel to (101) and (011) and are very similar to the layers of FeO6 octahedra in the spinel structure. Silicon is located in the sixfold coordination in I-Fe2SiO4. The transformation to the new high-pressure phase is reversible under decompression at ambient temperature. A martensitic transformation of each slab of the spinel structure with translation vector <1/8 over right arrow 1/8 over right arrow 1/8 over right arrow> generates the I-Fe2SiO4 structure. Laser heating of I-Fe2SiO4 at 1500 K results in a decomposition of the material to rhombohedral FeO and SiO2 stishovite.FeK beta X-ray emission measurements at high pressure up to 65 GPa show that the transition from a high spin (HS) to an intermediate spin (IS) state begins at 17 GPa in the spinel phase. The IS electron spin state is gradually enhanced with pressure. The Fe2+ ion at the octahedral site changes the ion radius under compression at the low spin, which results in the changes of the lattice parameter and the deformation of the octahedra of the spinel structure. The compression curve of the lattice parameter of the spinet is discontinuous at similar to 20 GPa. The spin transition induces an isostructural change.

Synthesis of Crystalline Beta-Fesi2 under High-Temperature and High-Pressure

EXPERIMENTAL STUDY ON THE PHASE RELATIONS OF THE SYSTEM Mg2SiO4-MgAl2O4 AT HIGH PRESSURE AND HIGH TEMPERATURE

High-pressure Synthesis of High-Performance Submicron-Sized Polycrystalline Β-Si3n4 Bulk Without Additives

Synthesis and Optical Properties of Semiconducting Beta-Fesi2 Nanocrystals

Phase Transformation Of Beta-Fesi2-Based Alloys Under In-Situ High-Temperature And High-Pressure X-Ray Diffraction Measurements

Crystal Structure and Phonon Density of States of FeSi up to 120 GPa

Crystallization Behavior of Amorphous Si2bc3n Ceramic Monolith Subjected to High Pressure

Formation of nanocrystalline Fe73.5Cu1Nb3Si13.5B9 alloy under high pressure

Phase transformation of /spl beta/-FeSi/sub 2/-based alloys under in-situ high-temperature and high-pressure X-ray diffraction measurements

High-Pressure and High-Temperature Synthesis and In Situ High-Pressure Synchrotron X-ray Diffraction Study of HfSi2

Synthesis of β-Si3N4 powder from quartz via carbothermal reduction nitridation

A New High-Pressure Phase of Fe2SiO4 and the Relationship Between Spin and Structural Transitions

Simultaneous High‐p, High‐t X Ray Diffraction Study of Β‐(mg,fe)2sio4 to 26 GPa and 900 K

Synthesis Of Beta-Fesi2 And Alpha-Fesi2 Phases By Fe Ion-Implantation Into Si Using Metal Vapor Vacuum-Arc Ion-Source

Formation of Nanocrystalline Fe 73.5 Cu 1 Nb 3 Si 13.5 B 9 Alloy under High Pressure

Porous silicon based <i>β</i>-FeSi<sub>2</sub> and photoluminescence

Effect of Si on the Growth Behavior of the Fe2Al5 Phase at Al-xSi(liquid)/Fe(solid) Interface During Holding by In-Situ Synchrotron Radiography

Porous silicon based β -FeSi 2 and photoluminescence

New Structure of High-Pressure Body-Centered Orthorhombic Fe2SiO4

Pressure-Induced Amorphization and Phase Transformations in Beta-Lialsio4

Coarse‐grained Β‐si3n4 Powders Prepared by Combustion Synthesis