Abstract:In this study, a novel technique of consecutive multi-pass cooperative lowered-temperature rolling (CMCLR) was proposed for the first time, with the purpose of preparing high performance wrought magnesium alloys. Based on this, a highly ductile magnesium alloy sheet could be effectively produced from ingot. The corresponding microstructure could directly evolve from coarse dendrites to equiaxed grains with an average size of similar to 5 mu m, which was attributed to the intense dynamic recrystallization (DRX) during isothermal deformation. The equivalent strain gradually decreased from the surface to the interior and edge of the rolled sheet due to the anisotropic plastic deformation. Instead, the temperature of the core of the sheet was slightly higher than that of the surface due to the deformation heat effect. The basal texture in the RD-TD plane generally weakened in the form of the splitting of basal texture toward the RD and the broadening of basal plane away from the pole center due to texture randomization dominated by DRXed grains. The exceptional ductility of more than 28.7% together with acceptable ultimate tensile strength of not less than 267 MPa was ascribed to the progressive work hardening as a result of seamless switching of multiple deformation modes, i.e., basal dislocation-slip-mediated deformation was preferentially operated and then was substituted by twinning-controlled deformation and non-basal dislocation-slip-dominated deformation. The selection of {10 (1) over bar2} twin variants agreed well with geometrical compatibility factor (m') criterion instead of Schmid's law. The activated twin variants nearly engulfed the whole parent grains for the sake of preserving compatible deformation continuity at ambient temperature, giving rise to the formation of TD-split texture. Comparatively, the {10 (1) over bar2} twinning could randomize the basal texture via reorienting grain orientations which in turn facilitated the reactivation of dislocation slip systems in the case of high temperature deformation.

Cavity Evolution Behavior of Twin-Roll-cast AZ31 Alloy Sheet During Hot Deformation

Cavity characteristics of twin-roll casting AZ31 magnesium alloy sheets during hot deformation

Deformation Microstructure and Characteristics of Cast-Rolling and Normal Rolling AZ31 Magnesium Alloy Sheets

Mechanical Behavior and Microstructure Evolution of a Rolled Magnesium Alloy AZ31B under Low Stress Triaxiality

Fracture Failure Analysis of Twin Rolling Casting Magnesium by Hot Compression

Towards revealing the relationship between deformation twin and fatigue crack initiation in a rolled magnesium alloy

Deformation failure behavior and fracture model of twin-roll casting AZ31 alloy under multiaxial stress state

Plastic Deformation and Fracture Mechanisms of Rolled Mg-8Gd-4Y-Zn and AZ31 Magnesium Alloys

In-situ Analysis of Microscopic Plastic and Failure Behaviors of Extruded Magnesium Alloy

Microstructure Evolution and Mechanical Behavior of AZ31 Magnesium Alloy Sheet with Bimodal Texture under Bending Deformation

Revealing the Microstructure Evolution Mechanism and Mechanical Responses of a Novel Al–Zn–Mg–Cu Alloy by Hot Deformation Process

Hot Deformation Behavior and Microstructural Evolution of Twin-Roll-Casting Mg Alloy during High-Temperature Compression

Cavity Behavior of SiCw/MB15 Magnesium Matrix Composites During Superplastic Deformation

Asymmetry in the hot deformation behavior of AZ31B magnesium sheets

Quasi-in Situ Electron Backscatter Diffraction Analysis of Twinning–detwinning Behavior in AZ31 Magnesium- Alloy Rolled Plates Subjected to Compression Loading in Different Directions

Superplastic Instability and Damage Evolution of AZ31B Magnesium Alloy Shee

Microstructure Evolution of AZ31B Magnesium Alloy Sheets Deformed in Different Deformation Directions

Microstructure of Asymmetric Twin-Roll Cast AZ31 Magnesium Alloy

An Exceptional Ductility of AZ31 Magnesium Alloy Sheet Achieved by Consecutive Multi-Pass Cooperative Lowered-Temperature Rolling

Microstructure and Texture Evolution of Mg-3Zn-1Al Magnesium Alloy During Large-Strain Electroplastic Rolling

The Dislocation-Twin Interaction and Evolution of Twin Boundary in AZ31 Mg Alloy