Abstract:The slip/twinning activity and cracking behavior of an extruded Mg-3Y sheet during strain-controlled tension-compression low-cycle fatigue (LCF) at room temperature were studied quantitatively and statistically by slip trace analysis and EBSD-based misorientation analysis combined with SEM. The twinned area fraction was 1.7 pct after 200 cycles indicating that twinning contributed limited plastic deformation, and only tension twins were observed. Among 989 grains analyzed, 11.4 pct grains exhibited observable slip traces. Basal slip, with a relative frequency of 81.4 pct, was the dominant deformation mode, and pyramidal II slip (12.4 pct) also exhibited a high activity. The slip-dominated deformation was responsible for the symmetrical hysteresis loops. Among the total 311 cracks observed after 200 cycles, 80.1 pct were intergranular and 19.9 pct were transgranular. The appearance of the two kinds of cracks was closely related. Persistent slip band (PSB, 13.8 pct) and twin (TW, 5.5 pct) were two key transgranular crack initiation sites. The PSB cracking fraction (cracked PSBs/total PSBs) for different slip modes followed pyramidal II (64 pct) > basal (36 pct) > prismatic (14 pct). Strain localization was likely to be responsible for the high cracking fraction of pyramidal II PSBs, which was consistent with their small normalized Schmid factors and the heterogeneous distribution of geometrically necessary dislocation density. Slip/Twinning transfers at grain boundary were also occasionally observed and they were closely associated with transgranular cracks.

Damage evolution of extruded magnesium alloy from deformation twinning and dislocation slipping in uniaxial stress-controlled low cycle fatigue

In-situ synchrotron X-ray tomography investigation of damage mechanism of an extruded magnesium alloy in uniaxial low-cycle fatigue with ratchetting

A mesoscopic damage model for the low-cycle fatigue of an extruded magnesium alloy

In Situ Monitoring of Dislocation, Twinning, and Detwinning Modes in an Extruded Magnesium Alloy under Cyclic Loading Conditions

Constitutive Modeling of Slip, Twinning and Detwinning for Mg Alloy and Inhomogeneous Evolution of Microstructure

Fatigue Damage Development in Extruded Mg-3al-Zn Magnesium Alloy

Statistical Analysis Of Grain-Scale Effects Of Twinning Deformation For Magnesium Alloys Under Cyclic Strain Loading

Effects of Initial {10-12} Twins on Cyclic Deformation and Fatigue of Magnesium Alloy at Low Strain Amplitudes

Quantitative Investigation on the Slip/Twinning Activity and Cracking Behavior During Low-Cycle Fatigue of an Extruded Mg-3Y Sheet

A Study of Fatigue Damage Development in Extruded Mg–Gd–Y Magnesium Alloy

Electron Backscatter Diffraction Observations of Twinning–detwinning Evolution in a Magnesium Alloy Subjected to Large Strain Amplitude Cyclic Loading

Cyclic Deformation And Correspondent Crack Initiation At Low-Stress Amplitudes In Mg-Gd-Y-Zr Alloy

Towards revealing the relationship between deformation twin and fatigue crack initiation in a rolled magnesium alloy

Quantitative analysis of the deformation modes and cracking modes during low-cycle fatigue of a rolled AZ31B magnesium alloy: The influence of texture

In-situ Analysis of Microscopic Plastic and Failure Behaviors of Extruded Magnesium Alloy

Cyclic Deformation and Fatigue of Extruded ZK60 Magnesium Alloy with Aging Effects

Mechanical Behavior and Microstructure Evolution of a Rolled Magnesium Alloy AZ31B under Low Stress Triaxiality

Microstructure evolution during high cycle fatigue in Mg-6Zn-1Mn alloy

Quantitative Investigation on the Deformation Modes and Cracking Behavior During Cyclic Torsional Loading of Extruded Pure Mg and Mg-3y Alloy

Cyclic Shear Deformation and Fatigue of Extruded Mg-Gd-Y Magnesium Alloy

Quantitative study on the influence of strain amplitude on deformation mechanisms and cracking modes during cyclic torsion of AZ31 magnesium alloy