Plasticity and Fracture Mechanism of Refine-Grain AZ31 Magnesium Alloys Sheet
bo jian wang,yao dan zhang,shan li
DOI: https://doi.org/10.4028/www.scientific.net/AMR.415-417.1096
2012-01-01
Abstract:In this paper, the microstructure and mechanical properties of refine-grain AZ31 magnesium alloy sheets was investigated upon annealing under different temperature. Plasticity and fracture mechanism of refine-grain AZ31 magnesium alloy sheet was discussed. magnesium alloy is expected to become the 21st century important commercial light structural materials, due to its small density (1.78 similar to 1.91g/cm(3)), high specific strength and stiffness, dimensional stability and high thermal conductivity,excellent mechanical process property[1].And compared with engineering plastics and high-strength fiber, magnesium alloy also has shock absorption, thermal conductivity, machinability and recycled, known as the 21st century "green" engineering materials currently, due to the structure characteristics of magnesium alloys, a large number of magnesium alloy products obtained by casting the production, but through extrusion, rolling, forging process such as production of magnesium alloy products performance is excellent, make it play a special use in different fields, which is an important and indispensable part in magnesium alloy material research and development field. The magnesium alloy plastic deformation ability is bad, so product its production has particularity and the difficulty. Generally [1,2], magnesium is hexagonal close packed(HCP) structure, limited slip systems at room temperature, resulting in magnesium and magnesium alloy is worse than the other common metal resulting in magnesium and magnesium alloy plastic deformation is worse than the other common metal. This experiment investigated influence of the cold-state wrought magnesium alloy AZ31 in different annealing temperature on the mechanical properties, plastic deformation, fracture mode and microstructure, that do basic research for fully understand the deformation behavior of wrought magnesium alloy and the further development of better performance magnesium alloys.