Abstract:The corrosion behavior of functionally graded cemented carbide (FGCC), with CoNiCrFe binder (WC-CoNiCrFe), has been investigated by performing electrochemical measurements and chemical characterization. The results showed that the CoNiCrFe binder was selectively dissolved in alkaline and acidic solutions. In the NaOH solution, the high contents of Ni and Co generated a passive film consisting of Co(OH) 2 , Ni(OH) 2 , Co 3 O 4 , and NiO that effectively isolated the corrosive medium from the materials. However, the contents of Fe and Cr were too low to provide satisfactory protection. In the HCl solution, the Cr element generated Cr 0 , Cr 2 O 3 , and Cr(OH) 3 . However, the Cr content was too low to form a passive film. In addition, Co, Ni and Fe in the binder were selectively dissolved in the acidic solution. Moreover, compared with the FGCC, the non-graded cemented carbide (CC) had a higher binder content and a more dispersed WC distribution. Thus, it formed a denser and thicker passive film, which was beneficial for the corrosion resistance in the NaOH solution. However, the CoNiCrFe binder was severely corroded in the HCl solution, which was due to the absence of a passive film. In comparison, the FGCC with a lower binder content and a denser WC distribution, showed a higher corrosion resistance. On the other hand, the WC grain size showed the opposite effect in alkaline and acidic solutions. In the NaOH solution, a small WC grain size increased the number of WC/CoNiCrFe interfaces, which favored the formation of a dense passive film. It, thereby reduced the probability for pitting corrosion. In the HCl solution, the corrosion generally started from grain boundaries with high interface energy as no passive film existed. Thus, a large WC grain size facilitated the improvement of the corrosion resistance. The results from the present study do not only provide a theoretical guidance for an understanding of the anticorrosion mechanism of WC-CoNiCrFe, but also a new approach for the preparation of cemented carbides with high corrosion resistance.

Preparation and Fatigue Properties of Functionally Graded Cemented Carbides

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Microstructures and mechanical properties of the bilayer functionally graded WC-TiC-Ni/Co cemented carbides

Oxidation behavior of functionally graded cemented carbides with CoNiFeCr multi-principal-element alloy binder

Corrosion behavior of functionally graded cemented carbides with CoNiCrFe binder

Study on the Properties of Coated Cutters on Functionally Graded WC-Co/Ni-Zr Substrates with FCC Phase Enriched Surfaces

Microstructure and Properties of Wcp/Cu Layered Functionally Graded Materials Prepared by Vacuum Hot-Pressed Sintering

Investigation for the Fracture Process of WCp/Cu Functionally Graded Materials under Three-Point-Bending

Fabrication and performance of graded ultrafine WC–Co cemented carbide tool by one/two-step spark plasma sintering

Preparation of a novel dual structure graded cemented carbides induced by bidirectional diffusion

Fracture behavior of cemented carbides with CoNiFe medium entropy alloy binder

Characterization and forming process of a functionally graded WC-Co/Ni composite

Synthesis of Functionally Graded AA7075-B4C Composite with Multi-Level Gradient Structure

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Synthesis, properties, and applications of functionally gradient cemented carbides

Two-material Powder Injection Molding of Functionally Graded WC–Co Components

Fabrication of W–Cu Functionally Graded Material with Improved Mechanical Strength

Fabrication and Micro-Structure of a Multilayer Functionally Graded (wc–co)–ni Composite

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Comparative Study on Microstructure and Mechanical Properties of Coarse-grained WC-based Cemented Carbides Sintered with Ultrafine WC or (W+C) as Additives

Novel design and composition optimization of self-lubricating functionally graded cemented tungsten carbide cutting tool material for dry machining