Abstract:Electron backscatter diffraction (EBSD) patterns can exhibit Kikuchi bands with inverted contrast due to anomalous absorption. This can be observed, for example, on samples with nanoscale topography, in case of a low tilt backscattering geometry, or for transmission Kikuchi diffraction (TKD) on thicker samples. Three examples are discussed where contrast-inverted physics-based simulated master patterns have been applied to find the correct crystal orientation. As the first EBSD example, self-assembled gold nanostructures made of Au fcc and Au hcp phases on single-crystal germanium were investigated. Gold covered about 12% of the mapped area, with only two-thirds being successfully interpreted using standard Hough-based indexing. The remaining third was solved by brute force indexing using a contrast-inverted master pattern. The second EBSD example deals with maps collected at a non-tilted surface instead of the commonly used 70 degree tilted one. As TKD example, a jet-polished foil made of duplex stainless steel 2205 was examined. The thin part close to the hole edge producing normal-contrast patterns were standard indexed. The areas of the foil that become thicker with increasing distance from the edge of the hole produce contrast-inverted patterns. They covered three times the evaluable area and were successfully processed using the contrast-inverted master pattern. In the last example, inverted patterns collected at a non-tiled sample were mathematically inverted to normal contrast, and Hough/Radon-based indexing was successfully applied.

Texture Analysis of Monofilamentary, Ag-sheathed (pb,bi)2sr2ca2cu3ox Tapes by Electron Backscatter Diffraction (EBSD)

Characterization of Microtexture in Bi-2223 Tapes Using Electron Back-Scatter Pattern Orientation Imaging

Investigation of Local Texture Correlations in Bi-2223 High Temperature Superconductor Tapes

EBSD Characterization of Specific Microstructures in RE-BCO Superconductors

Mechanical Properties Of (Bi,Pb)-2223 Multifilament Tapes With Ag-Alloy Sheath

Residual Stress/Strain Analysis of Bulk YBCO Superconductors Using EBSD

Local Orientation Variations in YBCO Films on Technical Substrates - A Combined SEM and EBSD Study

Preparation of C-Axis Textured Bi-2212 Thin Films on Silver Substrates by Using Chemical Solution Deposition

Investigation of Medium to High Strain Deformation Microstructures Using an Automated Electron Backscattering Pattern (EBSP) System

Cyclic Stress Measurement in a Microscopic Region Using EBSD Analysis of Grown Grains Occurred in the Copper Foil

Formation and Growth Studies of the (bi,pb)(2)sr2ca2cu3o10 Phase in Ag Sheathed Tapes

Research on the recrystallization texture evolution in rolled Ag by quasi-situ EBSD

EBSD and TKD analyses using inverted contrast Kikuchi diffraction patterns and alternative measurement geometries

Choice of Bi2223 Unit Cell for Texture Studies Using Orientation Determination in the Scanning Electron Microscope

Biaxially Textured (bi, Pb)(2)Sr2Ca2Cu3Ox Thin Films on LaAlO3 Substrates Fabricated Via the Chemical Solution Deposition Method

Homogeneity Study of Bi-2223/Ag Monofilamentary Tapes Using Hall Sensor Magnetometry

<i>In Situ</i> EBSD Study of Stable Cube Texture in an Advanced Composite Substrate Used in YBCO-Coated Conductors

Development and Evolution of Biaxial Texture of Rolled Nickel Tapes by Ion Beam Bombardment for High Tc Coated Conductors

Structural and Compositional Defects in High-J/sub C/ Bi-2223 Tapes

Fabrication and properties of some Ag-alloy sheathed Bi-2223 tapes

Microstructure of the ceramic in superconducting Bi-2223 composite tapes after bending strain cycles