Influence of Cr Deficiency on Sintering Character and Properties of SOFC Interconnect Material La0.7Ca0.3Cr1−xO3−δ

Songlin Wang,Mingfei Liu,Yingchao Dong,Kui Xie,Xingqin Liu,Guangyao Meng

DOI: https://doi.org/10.1016/j.materresbull.2007.10.039

IF: 5.6

2007-01-01

Materials Research Bulletin

Abstract:The SOFC interconnect materials La0.7Ca0.3Cr1−xO3−δ (x=0–0.09) were prepared using an auto-ignition process and characterized. XRD analysis indicated that all the samples displayed a pure perovskite phase after sintered at 1400°C for 4h. The relative density increased from 67% (x=0) to 95.8% (x=0.02) and reached to about 97% (x>0.02), as sintered at 1400°C for 4h. The electrical conductivity in air dramatically increased and then lowered slowly with x values. The sample with 0.03 Cr deficiency got a maximum conductivity of 61.7Scm−1 at 850°C in air, which is about three times as high as that of the sample with no Cr deficiency (20.6Scm−1). The sample with 0.06 Cr deficiency exhibited the highest electrical conductivity of 3.9Scm−1 at 850°C in pure H2. The thermal expansion coefficient (TEC) were below 11.8×10−6K−1 for samples of x=0.02–0.09, that was of well compatibility with other components in SOFCs. Results indicate that the materials with 0.02–0.06 Cr deficiency have high properties and are much suitable for SOFC interconnect.