Preparation and properties of ceramic interconnecting materials, La0.7Ca0.3CrO3-δ doped with GDC for IT-SOFCs

Xiaoliang Zhou,Jianjun Ma,Feijun Deng,Guangyao Meng,Xingqin Liu

DOI: https://doi.org/10.1016/j.jpowsour.2006.06.091

IF: 9.2

2006-01-01

Journal of Power Sources

Abstract:One of the challenges for improving the performance and cost-effectiveness of solid oxide fuel cells (SOFCs) is the development of effective interconnect materials. A widely used interconnect ceramic for SOFCs is doped lanthanum chromite. In this paper, we report a doped lanthanum chromite, La0.7Ca0.3CrO3−δ (LCC)+xwt.% Gd0.2Ce0.8O1.9 (GDC) (x=0–10), with improved electrical conductivity and sintering capability. In this composite material system, LCC+GDC were prepared by an auto-ignition process and the electrical conductivity was characterized in air and in H2. The LCC powders exhibited a better sintering ability and could reach a 94.7% relative density at 1400°C for 4h in air and with the increase of GDC content the relative density increased, reached 98.5% when the GDC content was up to 10wt.%. The electrical conductivity of the samples dramatically increased with GDC addition until a maximum of 134.48Scm−1 in air at 900°C when the materials contained 3wt.% GDC. This is 5.5 times higher than pure LCC (24.63Scm−1). For the sample with a 1wt.% GDC content, the conductivity in pure H2 at 900°C was a maximum 5.45Scm−1, which is also higher than that of pure LCC ceramics (4.72Scm−1). The average thermal expansion coefficient (TEC) increased with the increase of GDC content, ranging from 11.12 to 14.32×10−6K−1, the majority of which unfortunately did not match that of 8YSZ. The oxygen permeation measurement presented a negligible oxygen ionic conduction, indicating that it is still an electronically conducting ceramic. Therefore, it is a very promising interconnect material for higher performance and cost-effectiveness for SOFCs.