Abstract:In this study, the hybrid aluminum matrix composite reinforced with TiB2 and TiAl3 particles was fabricated by in situ synthesis. Hot compression tests were performed at a deformation temperature range of 300 - 450 celcius and strain rates of 0.001 - 1 s-1 on a Gleeble-350 0 system to investigate the hot deformation behavior of the fabricated composite. The experimental results show that the flow stress was sensitively dependent on the strain rate and temperature, and the peak stress level increased with the decrease of deformation temperature or the increase of strain rates. A sine-hyperbolic constitutive equation with the hot deformation activation energy of 244.844 kJ/mol was established to describe the flow stress of the composite. Further, the effects of TiB2 and TiAl3 particles on the flow stress levels of the composite under different hot deformation conditions were described by the developed strengthening model. It found that the predicting values of yield strength calculated by the established model agreed well with the experi-mental data, and the nano-sized TiB2 had a greater contribution to the stress level of the composite compared to the micro-sized TiAl3. Based on the microstructure characterization, dynamic recovery (DRV) was found to be the main flow softening mechanism during hot deformation and the evolution of dynamic recrystallization (DRX) was insufficient. Micro-sized TiAl3 particles and TiB2 particle clusters can promote DRX nucleation and growth of newly formed grains, meanwhile, separated nano-sized TiB2 particles had a pinning effect on the dislocation migration leading to substructure formation, which was in favor of the development of DRV.(c) 2022 Elsevier B.V. All rights reserved.

Microstructure Formation Mechanism of (al2o3+tib2+al3ti)/al Composites Fabricated by Reaction Hot Pressing

Microstructure Formation Mechanism of (al2o3+tib2+al3ti)/al Composites Fabricated by Reactive Hot Pressing

In Situ TiBw/Ti–6Al–4V Composites with Novel Reinforcement Architecture Fabricated by Reaction Hot Pressing

In Situal3ti–al2o3 Intermetallic Matrix Composite: Synthesis, Microstructure, and Compressive Behavior

Microstructural Characteristics and Evolution of Ti2AlN/TiAl Composites with a Network Reinforcement Architecture During Reaction Hot Pressing Process

Ti3alc2-Al2o3-Tial3 Composite Fabricated by Reactive Melt Infiltration

Microstructure of In-Situ Synthesized (tib+tic)/ti Composites Prepared by Hot-pressing

Synthesis and Mechanical Properties of TiB2/Ti2AlN Composites Fabricated by Hot Pressing Sintering

Design and Strengthening Behaviour of Ti2alc/Tial Composite by Low-Temperature Hot-Pressing Process

Fabrication of in Situ Ti 2 AlN/TiAl Composites by Reaction Hot Pressing and Their Properties

Microstructure and mechanical properties of Ti3(Al,Ga)C2/Al2O3 composites prepared by in situ reactive hot pressing

Microstructure and mechanical properties of reaction synthesized TiB/Ti-4.0Fe-7.3Mo composites by hot press sintering

Processing, Microstructural Characterization and Mechanical Properties of in Situ Ti3AlC2/TiAl3 Composite by Hot Pressing

Microstructural characterization and mechanical properties of TiAl–Al2Ti4C2–Al2O3–TiC in situ composites by hot-press-aided reaction synthesis

Microstructural Characters of TiAl Intermetallics Prepared with Different Processes

Evaluation of the microstructure of in-situ reaction processed Al3Ti-Al2O3-Al composite

Formation of A Tib2-Reinforced Copper-Based Composite by Mechanical Alloying and Hot Pressing

LOW CYCLE FATIGUE OF (Al2O3+TiB2+Al3Ti) /Al COMPOSITES FABRICATED BY REACTIVE HOT PRESSING

Microstructure and tensile behavior of novel laminated Ti-TiBw/Ti composites by reaction hot pressing

Investigation of the Hot Deformation Behavior and Microstructure Evolution of TiB2 +tial3/2024al Composite

Microstructural Characterisation Ofin Situtib/ti Matrix Composites Prepared by Mechanical Alloying and Hot Pressing