Abstract:In this work, the effects of Nb2O5 addition on the dielectric properties and phase formation of BaTiO3 were investigated. A core–shell structure was formed for Nb-doped BaTiO3 resulted from a low diffusivity of Nb5+ ions into BaTiO3 when grain growth was inhibited. In the case of 0.3–4.8 mol% Nb2O5 additions, two dielectric constant peaks were observed. The Curie dielectric peak was determined by the ferroelectric-paraelectric transition of grain core, whereas the secondary broad peak at lower temperature was due to strong chemical inhomogeneity in Nb-doped BaTiO3 ceramics. The dielectric constant peak at Curie temperature was markedly depressed with the addition of Nb2O5. On the other hand, the secondary dielectric constant peak was enhanced when sintered above 1280 °C for higher Nb2O5 concentrations (≥1.2 mol%). The Curie temperature was shifted to higher temperatures, whereas the transition temperature corresponding to the secondary peak moved to lower temperatures as increasing the amount of Nb2O5 more than 1.2 mol%. The decrease of this lower transition temperature was assumed to be closely related with the secondary phase formation when Nb concentration greater than 1.2 mol%. From XRD analyses, a large amount of secondary phases was observed when Nb2O5 amount exceeded 1.2 mol%. The coefficients of thermal expansion of Nb-doped BaTiO3 were increased with increasing Nb2O5 contents, resulting in large internal stress between cores and shells. Therefore, the shift of Curie temperature to higher temperatures was attributed to internal stress resulting from the formation of a core–shell structure and a large amount of secondary phase grains.

Study of Nb-Zn Co-Doped Ba(Ti,Zr)O-3 Ceramics

Low-Temperature Sintering and Microwave Dielectric Properties of Znzrnb2o8 Ceramics with Bacu(B2o5) Addition

Effects of Nb 2 O 5 Doping on the Microstructure and the Dielectric Temperature Characteristics of Barium Titanate Ceramics

Microstructure and Electric Properties of Nb Doping X(ba0.7ca0.3)tio3–(1−x)ba(zr0.2ti0.8)o3 Ceramics

Low Temperature Sintering and Microwave Dielectric Properties of Zr 0.3 (zn 1/3 Nb 2/3 ) 0.7 TiO 4 Ceramics Doped with CuO-B 2 O 3

Dielectric behaviors of Nb2O5–Co2O3 doped BaTiO3–Bi(Mg1/2Ti1/2)O3 ceramics

Large Piezoelectric Coefficient with Enhanced Thermal Stability in Nb5+-doped Ba0.85Ca0.15Zr0.1Ti0.9O3 Ceramics

Low-temperature Sintering of (co0.35zn0.65)tinb2o8 Temperature-Stable Microwave Dielectric Ceramics with BaCu(B2O5) Additions

Microstructure and dielectric properties of BaTiO3-Nb 2O5-Zn0.8Mg0.2TiO3 ternary system

Doping Behaviors of Nb2O5 and Co2O3 in Temperature Stable BaTiO3-based Ceramics

Influence of Ba–Zn–B Additives on the Sintering Behavior and Dielectric Properties of BaNd2Ti4O12 Ceramics

Effect of TiO 2 on Phase Composition and Microwave Dielectric Properties of Zn 1.01 Nb 2 O 6 Ceramics

Microstructure and Electrical Properties of Al<sub>2</sub>O<sub>3</sub>-Doped Ba<sub>0.9</sub>Ca<sub>0.1</sub>Ti<sub>0.8</sub>Zr<sub>0.2</sub>O<sub>3</sub> Based Dielectric Ceramics

EFFECT OF DOPING CaO ON DIELECTRIC PROPERTIES OF BaZr0.05Ti0.95O3 CERAMICS

Influence of BaZrO3, MnCO3 additives on dielectric properties and microstructure of Ba(Zn1/3Nb2/3)O3 ceramics and Ba(Zn1/3Nb2/3)O3-Sr(Zn1/3Nb2/3)O3 solid solutions

Low temperature sintering and microwave dielectric properties of BaO–0.6ZnO–2.9TiO 2 ceramics using BaCu(B 2 O 5 ) addition

Lead-free Ba0.98Ca0.02Zr0.02Ti0.98O3 ceramics with enhanced electrical performance by modifying MnO2 doping content and sintering temperature

Microwave Dielectric Properties of ZnO-2TiO 2 -Nb 2 O 5 Ceramics with BaCu (B 2 O 5 ) Addition

Effects of Y2O3 Substitution on Microwave Dielectric Properties of Ba(Co0.6Zn0.38)1/3Nb2/3O3 Ceramics

Low Temperature Sintering and Dielectric Properties of BaTi_(0.75)Zr_(0.25)O_3 Ceramic

Microstructure and Electrical Properties of Al2o3-Doped Ba0.9ca0.1ti0.8zr0.2o3 Based Dielectric Ceramics