Abstract:We report the ethylene glycol-mediated solvothermal synthesis of the continuous solid solution (Sb1-xBix)2S3 (0 < x < 1) with 1D nanostructures (nanowires and nanorods). The ternary products show a broad variation in Bi:Sb composition ratios (53:47–7:93), length-to-diameter aspect ratios (2.7–66.2), and optical bandgap energies (1.36–1.55 eV) as well as an enhanced photocurrent (e.g., (Sb1-xBix)2S3 with x = 0.22 is three times higher than pure Sb2S3). The gradual shift of peak positions in the XRD patterns and the uniform distributions of Bi, Sb and S elements in EDS mapping prove the formation of single-phase (Sb1-xBix)2S3 solid solution. Its formation is due to an isostructure-favored alloying mechanism, since Sb2S3 and Bi2S3 possess the same orthorhombic structure (space group: Pnma) and the similar lattice constants. The substitution of Bi for Sb isovalent cations can shorten the lengths of ternary alloyed Sb–Bi–S nanowires and transfer them to low aspect-ratio nanorods at high Bi/Sb precursor ratios. The dependence of the lengths on Bi/Sb ratios is reasonably interpreted considering the differences in the number of nuclei at different amounts of Bi ions and the covalency of Bi–S and Sb–S bonds during the alloying process.

Scalable Synthesis of A2S3 (a=sb, Bi) Submicro/nanowires Using Their Powders Via Solvothermal Proceeding

Solvothermal Synthesis of Sb2S3 Nanowires on a Large Scale

Synthesis And Characterization Of Sb2s3 Nanowires

A solvothermal decomposition process for fabrication and particle sizes control of Bi<sub>2</sub>S<sub>3</sub> nanowires

Long Bi2s3 Nanowires Prepared by A Simple Hydrothermal Method

A solvothermal decomposition process for fabrication and particle sizes control of Bi 2 S 3 nanowires

Control to Synthesize Bi2s3 Nanowires by A Simple Inorganic-Surfactant-Assisted Solvothermal Process

Length and composition tunable Sb–Bi–S nanowires for optoelectronic devices prepared via an isostructure-favored solvothermal synthesis

Hydrothermal Synthesis Ultralong Single-crystal Sb 2 S 3 Nanowires

Growth of Single-Crystal Sb2S3 Nanowires Via Solvothermal Route

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

Solvothermal synthesis of antimony nanowire bundles, tube-groove-like nanostructures and dendrites

Solvothermal Preparation of Sb2Se3 Nanowires

Facile Synthesis of Bi2s3 Nanowire Arrays

Large‐Scale Synthesis of Ultralong Bi2S3 Nanoribbons Via a Solvothermal Process

Growth of Single-Crystal Sb2S3 Nanorods, Dendrites and Straw-Tied-like Architectures Via a Precursor–solvothermal–pyrolysis Route

Hydrothermal synthesis of M2S3 (M = Sb, Bi) bulk single crystals and nanorods

Preparation of Shuttle‐like Sb2S3 Nanorod‐bundles Via a Solvothermal Approach under Alkaline Condition

Synthesis and Growth Mechanism of Bi2S3 Nanoribbons

Preparation and Characterisation of Single-Crystalline Structure Sb/Bi2te3 Superlattice Nanowires

Scalable Synthesis of Sb(III)Sb(V)O4 Nanorods from Sb2O5 Powder Via Solvothermal Processing