Abstract:The CdS nanowires were synthesized by a solvothermal method in ethylenediamine solvent both at short time (2 h) and longer time (more than 12 h). The nanowires had an average diameter of ca. 26 nm with a length of ca. 1-3 mu m at 200 degrees C for 2 h and similar to 43 nm in diameter and similar to 4-6 mu m in length at 200 degrees C for 12 h, respectively. These CdS nanowires were in crystalline wurtzite structure, and their crystal growth direction was [0001]. An interesting phenomenon was found that the nanowires synthesized at 2 h broken into nanorods with increasing reaction time. These broken nanorods grew into nanowires at 12 h again. More than 12 h, the diauxic growth nanowires become longer and little thicker without other obvious changes. Based on a series of experimental results, it was revealed that the formation of CdS nanowires followed a novel diauxic growth processes during the hydrothermal synthesis: (1) the formation of nanowhiskers on chrysanthemum-like nanostructure as seeds for 1-D nanostructure, (2) transformation of nanowhiskers into the CdS nanorods on the surface of chrysanthemum-like nanostructures, (3) growth of CdS nanowires from CdS nanorods, (4) broken of CdS nanowire into short CdS nanorods and (5) diauxic growth of CdS nanowires from CdS nanorods preferentially along the c-axis again.

Solvothermal Synthesis of Sb2S3 Nanowires on a Large Scale

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

Ultrafast growth of single-crystalline Si nanowires

Solvothermal synthesis of antimony nanowire bundles, tube-groove-like nanostructures and dendrites

A solvothermal decomposition process for fabrication and particle sizes control of Bi<sub>2</sub>S<sub>3</sub> nanowires

A solvothermal decomposition process for fabrication and particle sizes control of Bi 2 S 3 nanowires

Large‐Scale Production of NbS2 Nanowires and Their Performance in Electronic Field Emission

Long Bi2s3 Nanowires Prepared by A Simple Hydrothermal Method

Controllable Growth of Se Nanotubes and Nanowires from Different Solvent During the Sonochemical Process

Growth of Crystalline Sb2S3 Nanorods by Hydrothermal Method

Sonochemical Synthesis of Amorphous Long Silver Sulfide Nanowires

Synthesis and Formation Mechanism of Bi(Se,S) Nanowires Via A Solvothermal Template Process

Large scale synthesis of uniform CuS nanotubes in ethylene glycol by a sacrificial templating method under mild conditions

Hydrothermal synthesis of nanowires ZnS with surfactant

Good Optical Properties of Branched CdS Nanoparticles and Its Large Area Growth via Solvothermal Route

High Yield CdS Nanowires Synthesized by Solvothermal Routes and Novel Diauxic Growth Mechanism

Low-Temperature Synthesis of Single Crystalline Ag2S Nanowires on Silver Substrates

Catalytic Synthesis of Long NbS2 Nanowire Strands

A Simple Solution Route to Single-Crystalline Sb<sub>2</sub>O<sub>3</sub>Nanowires with Rectangular Cross Sections

Hydrothermal synthesis of M2S3 (M = Sb, Bi) bulk single crystals and nanorods

High-quality Ultralong Sb2S3 Nanoribbons on Large Scale.