Synthesis And Characterization Of Sb2s3 Nanowires

Liu Yun,Miao Hongyan,Tan Guoqiang,Zhu Gangqiang

DOI: https://doi.org/10.3321/j.issn:1002-185X.2008.03.022

2008-01-01

Rare Metal Materials and Engineering

Abstract:Using Na2S and SbCl3 as raw materials and adopting the hydrothermal method, a great number of Sb2S3 nanowires with the higher length diameter ratio have been prepared after 12 hours reaction at 240 degrees C. X rays powder diffraction testing results reveal that the prepared product is the orthogonal Sb2S3 crystal phase, whose unit cell parameters are as follows: a=1.123 nm, b=1.131 nm, c=0.3840 nm. The analyses from SEM, TEM and HRTEM show that the prepared Sb2S3 nanowires is single crystal and grows along the [001] crystal face, whose diameter is between 100 and 250 nm and whose length is up to 100 mu m. This article has tentatively discussed the growth mechanism of Sb2S3 nanometer line.