Abstract:We report the ethylene glycol-mediated solvothermal synthesis of the continuous solid solution (Sb1-xBix)2S3 (0 < x < 1) with 1D nanostructures (nanowires and nanorods). The ternary products show a broad variation in Bi:Sb composition ratios (53:47–7:93), length-to-diameter aspect ratios (2.7–66.2), and optical bandgap energies (1.36–1.55 eV) as well as an enhanced photocurrent (e.g., (Sb1-xBix)2S3 with x = 0.22 is three times higher than pure Sb2S3). The gradual shift of peak positions in the XRD patterns and the uniform distributions of Bi, Sb and S elements in EDS mapping prove the formation of single-phase (Sb1-xBix)2S3 solid solution. Its formation is due to an isostructure-favored alloying mechanism, since Sb2S3 and Bi2S3 possess the same orthorhombic structure (space group: Pnma) and the similar lattice constants. The substitution of Bi for Sb isovalent cations can shorten the lengths of ternary alloyed Sb–Bi–S nanowires and transfer them to low aspect-ratio nanorods at high Bi/Sb precursor ratios. The dependence of the lengths on Bi/Sb ratios is reasonably interpreted considering the differences in the number of nuclei at different amounts of Bi ions and the covalency of Bi–S and Sb–S bonds during the alloying process.

Control to Synthesize Bi2s3 Nanowires by A Simple Inorganic-Surfactant-Assisted Solvothermal Process

Ultrafast growth of single-crystalline Si nanowires

Long Bi2s3 Nanowires Prepared by A Simple Hydrothermal Method

Hydrothermal synthesis of nanowires ZnS with surfactant

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

Surfactant-assisted solvothermal synthesis of Bi2S3 nanorods

A solvothermal decomposition process for fabrication and particle sizes control of Bi<sub>2</sub>S<sub>3</sub> nanowires

A solvothermal decomposition process for fabrication and particle sizes control of Bi 2 S 3 nanowires

Length and composition tunable Sb–Bi–S nanowires for optoelectronic devices prepared via an isostructure-favored solvothermal synthesis

Syntheses, Growth Mechanism, and Optical Properties of [001] Growing Bi2S3 Nanorods

Shape-Controlled Synthesis of Mnwo4 Nanocrystals by A Surfactant-Free Hydrothermal Method

Solvothermal Synthesis of Sb2S3 Nanowires on a Large Scale

Aqueous Chemical Reduction Synthesis of Bi2te3 Nanowires with Surfactant Assistance

High-Temperature Growth of Silica Sheathed Bi2s3 Semiconductor Nanowires

Hydrothermal Synthesis of Flower-Like Bi2S3with Nanorods in the Diameter Region of 30 Nm

Uniform Bi2S3 Nanowires: Structure, Growth, and Field-Effect Transistors

Synthesis and Formation Mechanism of Bi(Se,S) Nanowires Via A Solvothermal Template Process

Synthesis of InAs nanowires via a low-temperature solvothermal route.

A Simple and Effective Route for the Synthesis of Crystalline Silver Nanorods and Nanowires

Synthesis and Characterization of Nanocrystalline Bi2Se3 by Solvothermal Method

Synthesis and Evolution of PbS Nanocrystals Through a Surfactant-Assisted Solvothermal Route.