Abstract:We report the ethylene glycol-mediated solvothermal synthesis of the continuous solid solution (Sb1-xBix)2S3 (0 < x < 1) with 1D nanostructures (nanowires and nanorods). The ternary products show a broad variation in Bi:Sb composition ratios (53:47–7:93), length-to-diameter aspect ratios (2.7–66.2), and optical bandgap energies (1.36–1.55 eV) as well as an enhanced photocurrent (e.g., (Sb1-xBix)2S3 with x = 0.22 is three times higher than pure Sb2S3). The gradual shift of peak positions in the XRD patterns and the uniform distributions of Bi, Sb and S elements in EDS mapping prove the formation of single-phase (Sb1-xBix)2S3 solid solution. Its formation is due to an isostructure-favored alloying mechanism, since Sb2S3 and Bi2S3 possess the same orthorhombic structure (space group: Pnma) and the similar lattice constants. The substitution of Bi for Sb isovalent cations can shorten the lengths of ternary alloyed Sb–Bi–S nanowires and transfer them to low aspect-ratio nanorods at high Bi/Sb precursor ratios. The dependence of the lengths on Bi/Sb ratios is reasonably interpreted considering the differences in the number of nuclei at different amounts of Bi ions and the covalency of Bi–S and Sb–S bonds during the alloying process.

Large‐Scale Synthesis of Ultralong Bi2S3 Nanoribbons Via a Solvothermal Process

High-quality Ultralong Sb2S3 Nanoribbons on Large Scale.

High-Quality Ultralong Sb<sub>2</sub>S<sub>3</sub>Nanoribbons on Large Scale

Single‐Crystalline V2O5 Ultralong Nanoribbon Waveguides

High-Quality Ultralong Sb<sub>2</sub>Se<sub>3</sub>and Sb<sub>2</sub>S<sub>3</sub>Nanoribbons on a Large Scale via a Simple Chemical Route

Long Bi2s3 Nanowires Prepared by A Simple Hydrothermal Method

High-quality ultralong Sb2Se3 and Sb2S3 nanoribbons on a large scale via a simple chemical route.

Solvothermal Synthesis of Sb2S3 Nanowires on a Large Scale

Microwave-Assisted Solvothermal Synthesis of Radial ZnS Nanoribbons

A solvothermal decomposition process for fabrication and particle sizes control of Bi<sub>2</sub>S<sub>3</sub> nanowires

Length and composition tunable Sb–Bi–S nanowires for optoelectronic devices prepared via an isostructure-favored solvothermal synthesis

Hydrothermal Synthesis of Flower-Like Bi2S3with Nanorods in the Diameter Region of 30 Nm

A solvothermal decomposition process for fabrication and particle sizes control of Bi 2 S 3 nanowires

Surfactant-assisted solvothermal synthesis of Bi2S3 nanorods

Large-scale Polyol Synthesis of Single-Crystal Bismuth Nanowires and the Role of NaOH in the Synthesis Process

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

High-Pressure Synthesis of Single-Crystalline SnS Nanoribbons

High-quality ultralong Bi2S3 nanowires: structure, growth, and properties

Hollow Microscale Organization of Bi2s3 Nanorods

Single-Crystalline Sns2 Nano-Belts Fabricated by A Novel Hydrothermal Method

Solution-phase template approach for the synthesis of Cu<sub>2</sub>S nanoribbons