Abstract:Regular stibnite (Sb2S3) nanorods with diameters of 20-40 nm and lengths of 220-350 nm have been successfully synthesized by a sonochemical method under ambient air from an ethanolic solution containing antimony trichloride and thioacetamide. The as-prepared Sb2S3 nanorods are characterized by employing techniques including X-ray powder diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, energy-dispersive X-ray analysis, transmission electron microscopy, selected area electron diffraction, high-resolution transmission electron microscopy, and optical diffuse reflection spectroscopy. Microstructural analysis reveals that the Sb2S3 nanorods crystallize in an orthorhombic structure and predominantly grow along the (001) crystalline plane. High-intensity ultrasound irradiation plays an important role in the formation of these Sb2S3 nanorods. The experimental results show that the sonochemical formation of stibnite nanorods can be divided into four steps in sequence: (1) ultrasound-induced decomposition of the precursor, which leads to the formation of amorphous Sb2S3 nanospheres; (2) ultrasound-induced crystallization of these amorphous nanospheres and generation of nanocrystalline irregular short rods; (3) a crystal growth process, giving rise to the formation of regular needle-shaped nanowhiskers; (4) surface corrosion and fragmentation of the nanowhiskers by ultrasound irradiation, resulting in the formation of regular nanorods. The optical properties of the Sb2S3 amorphous nanospheres, irregular short nanorods, needle-shaped nanowhiskers, and regular nanorods are investigated by diffuse reflection spectroscopic measurements, and the band gaps are measured to be 2.45, 1.99, 1.85, and 1.94 eV, respectively.

Scalable Synthesis of Sb(III)Sb(V)O4 Nanorods from Sb2O5 Powder Via Solvothermal Processing

Preparation of Shuttle‐like Sb2S3 Nanorod‐bundles Via a Solvothermal Approach under Alkaline Condition

Synthesis and Photoelectrocatalytic Performance of Sb2S3 Nanorods from Natural Stibnite

Facile Solvothermal Synthesis of Single-Crystalline Bi2S3 Nanorods on a Large Scale

Good Optical Properties of Branched CdS Nanoparticles and Its Large Area Growth via Solvothermal Route

Synthesis of Magnesium Borate Nanorods by Sol-Gel Process

Preparation And Characterization Of Bismuth Sulfide Single Crystal Nanorods In Ionic Liquids

Pii: s0025-5408(01)00734-6

Growth of Single-Crystal Sb2S3 Nanorods, Dendrites and Straw-Tied-like Architectures Via a Precursor–solvothermal–pyrolysis Route

Synthesis of Ultrafine Lanthanum Hydroxide Nanorods by A Simple Hydrothermal Process

Growth of Crystalline Sb2S3 Nanorods by Hydrothermal Method

Surfactant-assisted solvothermal synthesis of Bi2S3 nanorods

Sonochemical Fabrication And Characterization Of Stibnite Nanorods

Hydrothermal Synthesis of Flower-Like Bi2S3with Nanorods in the Diameter Region of 30 Nm

A rational route to synthesize Bi2S3 nanorods in large scale

Low-temperature synthesis and characterization of β-La2S3 nanorods

Synthesis of Single Crystalline CdS Nanorods by a PVP-assisted Solvothermal Method

Synthesis of Novel Sbsi Nanorods by A Hydrothermal Method

Facile synthesis via a solvent molecular template and formation mechanism of uniform zinc antimony nanorods

A Simple Solution Route to Single-Crystalline Sb<sub>2</sub>O<sub>3</sub>Nanowires with Rectangular Cross Sections

Large-scale synthesis of uniform urchin-like patterns of Bi2S3 nanorods through a rapid polyol process