Abstract:In this paper,the selenium nanowires were synthesized with the sonochemical approach.The result of field-emission scanning electron microscopy(FESEM)shows that the as-prepared selenium nanowires are relatively uniform and abundant.Transmission electron microscopy(TEM)and X-rays diffraction(XRD)were further adopted to characterize the structure of the as-prepared Se products.The results of high-resolution TEM and XRD prove that the as-prepared selenium nanowires are single crystalline in nature and [001] oriented.The UV-vis absorption spectra of the selenium nanowires is determined at 671 nm,and the calculated forbidden energy gap is 1.66 eV.Based on a series of growth processes,a possible growth mechanism of the selenium nanowires was also proposed as follows:Se powders dissolve in the solution and generate free selenium atoms;then,selenium atoms recrystallize and form crystalline t-Se nuclei when the concentration of selenium atoms is high enough;the continuous feeding of selenium atoms onto the crystalline seeds leads to the formation of linear nanostructures due to the anisotropic crystal structure.In addition,the dissolution and sequential recrystallization make α-Se transform into more stable t-Se.Ultrasonic can provide proper energy to adjust the dynamics equilibrium of dissolution and recrystallization,thus accelerate its transformation.

Solvothermal Preparation of Sb2Se3 Nanowires

Solvothermal Synthesis of Sb2S3 Nanowires on a Large Scale

Synthesis and Formation Mechanism of Bi(Se,S) Nanowires Via A Solvothermal Template Process

Hydrothermal Synthesis and Characterization of Sb2Se3 Nanowires

One-Pot Synthesis of Sb2se3 Nanowires Using Selenium Dioxide As the Selenium Precursor in Air and Their Characterization

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

Polyol method synthesis and characterization of nanoscale Sb2Se3 wires

Controllable Growth of Se Nanotubes and Nanowires from Different Solvent During the Sonochemical Process

Polyol process preparation and characterization of Sb2Se3 nanowires

Preparation and Characterization of Wire-Like Sb2Se3 and Flake-Like Bi2Se3 Nanocrystals

Synthesis and Characterization of Hollow Sb2Se3 Nanospheres

Colloidal synthesis and characterization of single-crystalline Sb2Se3 nanowires

Preparation of Ultra-Long Sb2Se3 Nanoribbons Via a Short-Time Solvothermal Process

Solvothermal Route to Semiconductor Nanowires

Synthesis and Characterization of SnSe Nanowires by Solvothermal Method

Solvothermal Synthesis to Nanocrystalline Ni0.85Se and NiSe2 at Low Temperature.

Solvothermal route to Bi3Se4 nanorods at low temperature

Properties and characterization of Cu3SbS3 nanowires synthesized by solvothermal route

Hydrothermal Synthesis Ultralong Single-crystal Sb 2 S 3 Nanowires

Sonochemical Approach to Synthesis of Selenium Nanowires

One-dimensional Sb2Se3 nanostructures: Solvothermal synthesis, growth mechanism, optical and electrochemical properties