Abstract:Transverse mechanical properties of titanium matrix composites (TMCs) play an important role during its engineering service. Although SiCf / TC17 composite is one of the most promising TMC candidates for aeroengine, as we know its transverse properties have not been reported yet until now. In this work, the transverse strength of single SiC fiber reinforced TC17 composite was evaluated using cruciform specimen. The surface and cross-section of fractured specimen were investigated by SEM to determine the failure position during tensile test. Finite element simulation method was also used to analyze the mechanism of interfacial failure and crack propagation. During the transverse tensile test of single fiber specimen, the initial non-linearity in the stress-strain curve occurred at the stress of (271 +/- 12) MPa, which indicated the beginning of fiber-matrix interface failure. SEM observation showed that the crack in the center of sample appeared at the interface of reaction layer and carbon coating with a 24 degrees similar to 68 degrees angle to the applied loading direction and its length extended with the increase of the applied stress. The finite element simulation results based on bilinear cohesive element model showed that transverse fracture of composite interface was shear failure mode, which agreed well with the test results. Before the occurrence of non-linearity in the stress-strain curve, the crack initiated at the circular interface between reaction layer and carbon coating with a 40 degrees similar to 50 degrees angle to the applied loading direction. Crack initiation locations in test samples were different with those in simulation samples, because the actual composite interface was rough and some micro-flaws formed in the interface, whereas it was assumed to be an ideal rigid interface for simulation. Then the crack propagated along both circumferential and axial directions because of the shear stress. With the crack growing, the interface close to 0 degrees angle to the applied loading direction failed first caused by the radial tensile stress, whereas the interface near 90 degrees failed later as a result of circumferential shear stress. After complete failure of the interface, stress redistribution occurred around the SiC fiber and the interface separation increased with the increasing of the applied load, which gave rise to the yielding and deforming of the matrix near fiber until the final fracture of the composite.

Measurement and Evaluation of the Tensile Strength of Chinese CVD SiC Fibers

Measurement and Evaluation of the Tensile Strength of CVD SiC Fibers with Carbon Coating

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Study on the Mechanical Property of High‐Performance Silicon Carbide Fiber

Effect of CVI SiC interphase on tensile properties of SiC fibers with different surfaces

Study of SiC fiber axial compressive behavior using tensile recoil measurement

Effect of heat treatment on the microstructure and properties of CVD SiC fiber

Tensile Test of Unidirectional C_f/SiC Composites

Tensile Property of SiC_f/TC17 Composite at Room Temperature

Study on Tensile Behavior of Sicf/Tc17 Composites

Research on Single SiC Fiber Reinforced TC17 CompositesUnder Transverse Tension

Room and elevated temperature tensile properties of SiCf/TCl7 composite

Study of Strength and Its Reliability of SiC Fiber Bundle by Experimental and Monte-Carlo Simulation Approach

Tensile behavior of the designed SiCf/Ti2AlNb/Ti17 composites

Experimental and Numerical Investigations of Tensile Properties of SiC Particle‐Reinforced Composites

Unveil the Size-Dependent Mechanical Behaviors of Individual Cnt/Sic Composite Nanofibers by in Situ Tensile Tests in Sem

Interfacial Mechanical Properties of the Domestic 3rd Generation 2.5D SiCf/SiC Composite

Dataset on fractographic analysis of various SiC-based fibers

FRACTURE BEHAVIOUR OF SiC WHISKER REINFORCED Al COMPOSITES

STUDY OF THE TENSILE PROPERTIES OF DOMESTIC CARBON FIBERS

Microstructure and Mechanical Properties of SiC F /sibcn Ceramic Matrix Composites