Abstract:Transverse mechanical properties of titanium matrix composites (TMCs) play an important role during its engineering service. Although SiCf / TC17 composite is one of the most promising TMC candidates for aeroengine, as we know its transverse properties have not been reported yet until now. In this work, the transverse strength of single SiC fiber reinforced TC17 composite was evaluated using cruciform specimen. The surface and cross-section of fractured specimen were investigated by SEM to determine the failure position during tensile test. Finite element simulation method was also used to analyze the mechanism of interfacial failure and crack propagation. During the transverse tensile test of single fiber specimen, the initial non-linearity in the stress-strain curve occurred at the stress of (271 +/- 12) MPa, which indicated the beginning of fiber-matrix interface failure. SEM observation showed that the crack in the center of sample appeared at the interface of reaction layer and carbon coating with a 24 degrees similar to 68 degrees angle to the applied loading direction and its length extended with the increase of the applied stress. The finite element simulation results based on bilinear cohesive element model showed that transverse fracture of composite interface was shear failure mode, which agreed well with the test results. Before the occurrence of non-linearity in the stress-strain curve, the crack initiated at the circular interface between reaction layer and carbon coating with a 40 degrees similar to 50 degrees angle to the applied loading direction. Crack initiation locations in test samples were different with those in simulation samples, because the actual composite interface was rough and some micro-flaws formed in the interface, whereas it was assumed to be an ideal rigid interface for simulation. Then the crack propagated along both circumferential and axial directions because of the shear stress. With the crack growing, the interface close to 0 degrees angle to the applied loading direction failed first caused by the radial tensile stress, whereas the interface near 90 degrees failed later as a result of circumferential shear stress. After complete failure of the interface, stress redistribution occurred around the SiC fiber and the interface separation increased with the increasing of the applied load, which gave rise to the yielding and deforming of the matrix near fiber until the final fracture of the composite.

Tensile Test of Unidirectional C_f/SiC Composites

Research on Single SiC Fiber Reinforced TC17 CompositesUnder Transverse Tension

Study on the Mechanical Property of High‐Performance Silicon Carbide Fiber

Unveil the Size-Dependent Mechanical Behaviors of Individual Cnt/Sic Composite Nanofibers by in Situ Tensile Tests in Sem

Tensile Property of SiC_f/TC17 Composite at Room Temperature

A Combined Investigation of Bending Behavior of a SiC Fiber‐Reinforced Titanium Matrix Composite with Compressive and Tensile Tests

In-situ study of the fracture behavior of SiCf/SiC composite material under three-point bending

Microstructure and mechanical properties of SiC f /SiC composite prepared by chemical vapor infiltration

High-temperature tensile behavior of 3D SiC/SiC composites

Interface structure and tensile failure behaviour of novel SiC f /Ti–Ti 2 AlNb hybrid laminated composite material

Effect of Ultrasonic Vibration Tensile on the Mechanical Properties of High-Volume Fraction SiCp/Al Composite

Failure Modes and Toughening Mechanisms in CMC

Tensile behavior of the designed SiCf/Ti2AlNb/Ti17 composites

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Experimental and Numerical Study on the Bending Behavior of Satin-Woven SiCf/SiC Composites

Measurement and Evaluation of the Tensile Strength of CVD SiC Fibers with Carbon Coating

Study of Interfacial Stress Distribution in SiC Fiber Reinforced Titanium Matrix Composites on Transverse Tensile Tests

Study of SiC fiber axial compressive behavior using tensile recoil measurement

Experimental Study of High-Temperature Tensile Mechanical Properties of 3D Needled C/C–SiC Composites

In-situ Tensile Damage and Fracture Behavior of PIP SiC/SiC Minicomposites at Room Temperature

Phase‐field Simulation of Microscale Crack Propagation/deflection in SiCf/SiC Composites with Weak Interphase