Abstract:Transverse mechanical properties of titanium matrix composites (TMCs) play an important role during its engineering service. Although SiCf / TC17 composite is one of the most promising TMC candidates for aeroengine, as we know its transverse properties have not been reported yet until now. In this work, the transverse strength of single SiC fiber reinforced TC17 composite was evaluated using cruciform specimen. The surface and cross-section of fractured specimen were investigated by SEM to determine the failure position during tensile test. Finite element simulation method was also used to analyze the mechanism of interfacial failure and crack propagation. During the transverse tensile test of single fiber specimen, the initial non-linearity in the stress-strain curve occurred at the stress of (271 +/- 12) MPa, which indicated the beginning of fiber-matrix interface failure. SEM observation showed that the crack in the center of sample appeared at the interface of reaction layer and carbon coating with a 24 degrees similar to 68 degrees angle to the applied loading direction and its length extended with the increase of the applied stress. The finite element simulation results based on bilinear cohesive element model showed that transverse fracture of composite interface was shear failure mode, which agreed well with the test results. Before the occurrence of non-linearity in the stress-strain curve, the crack initiated at the circular interface between reaction layer and carbon coating with a 40 degrees similar to 50 degrees angle to the applied loading direction. Crack initiation locations in test samples were different with those in simulation samples, because the actual composite interface was rough and some micro-flaws formed in the interface, whereas it was assumed to be an ideal rigid interface for simulation. Then the crack propagated along both circumferential and axial directions because of the shear stress. With the crack growing, the interface close to 0 degrees angle to the applied loading direction failed first caused by the radial tensile stress, whereas the interface near 90 degrees failed later as a result of circumferential shear stress. After complete failure of the interface, stress redistribution occurred around the SiC fiber and the interface separation increased with the increasing of the applied load, which gave rise to the yielding and deforming of the matrix near fiber until the final fracture of the composite.

Study on Tensile Behavior of Sicf/Tc17 Composites

Room and elevated temperature tensile properties of SiCf/TCl7 composite

Research on Single SiC Fiber Reinforced TC17 CompositesUnder Transverse Tension

Tensile behavior of the designed SiCf/Ti2AlNb/Ti17 composites

Temperature Effects on Transverse Failure Modes of Carbon Fiber/bismaleimides Composites

Tensile Property of SiC_f/TC17 Composite at Room Temperature

Multiscale Failure Mechanism Analysis of SiC Fiber-Reinforced TC17 Composite Subjected to Transverse Tensile Loading at Elevated Temperature

High-temperature tensile behavior of 3D SiC/SiC composites

FEM Analysis of the Stress Response and Failure Mechanism of SiC-coated Cf/ SiC Composites During Thermal Shock

Fracture Toughness Evolution and Failure Mechanisms of Two-Dimensional SiCf/SiC Composites at Temperatures Up to 1500 °C in Air

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Tensile Behavior of 2D-C/sic Composites at Elevated Temperatures: Experiment and Modeling

Study on Fracture Behavior of SiCp/A356 Composites

Tensile Performance of 3D-C/sic Composites at High Temperature

Tensile Fatigue of a 2.5D-C/sic Composite at Room Temperature and 900°C

Experimental Study of High-Temperature Tensile Mechanical Properties of 3D Needled C/C–SiC Composites

Tensile Creep Properties and Damage Mechanisms of 2D-Sicf/sic Composites Reinforced with Low-Oxygen High-Carbon Type SiC Fiber

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

Damage accumulation during high temperature fatigue of Ti/SiCf metal matrix composites under different stress amplitudes

Study of SiC fiber axial compressive behavior using tensile recoil measurement

Influence of Depositiontemperature on Tensile Behavior and Fracture Characteristics of Sic Filament by Chemical Vapor Deposition