WANG Qu-dong,Chen Yong-jun,CHEN Wen-zhou,WEI Yin-hong,ZHAI Chun-quan,DING Wen-jiang

DOI: https://doi.org/10.3321/j.issn:1006-2467.2005.07.020

2005-01-01

Abstract:In situ three-layer surface composites of Zn-27Al-9.8Mg-5.2Si and Zn-27Al-6.3Mg-3.7Si alloys were obtained by centrifugal casting with preheated metal mould, which possesses the microstructures of accumulated lots of blocky primary Mg_2Si and a litter blocky primary Si in inner layer, accumulated primary Mg_2Si and primary Si in outer layer, and without primary Mg_2Si and primary Si in middle layer. The effects of composition, mold temperature, rotating rate and modification on microstructures of centrifugally cast Zn-27Al-Mg-Si alloys were investigated. The results show that the inner and outer layers of Zn-27Al-9.8Mg-5.2Si alloy are respectively thicker than those of Zn-27Al-6.3Mg-3.7Si alloy and have more primary Mg_2Si. During the centrifugal casting of Zn-27Al-6.3Mg-3.7Si alloy, with rotating rate increasing, the thickness of the inner layer increases and the outer layer becomes thinner and the addition of Na-salt can refine grain and primary Mg_2Si, and make primary Mg_2Si distribute more evenly and make primary Si nodular. Moreover, the forming process of composites was also analyzed.