Abstract:A new Mg-2.2 wt% Zn alloy containing 1.8 wt% Ca and 0.5 wt% Mn has been developed and subjected to extrusion under different extrusion parameters. The finest (~ 0.48 μm) recrystallized grain structures, containing both nano-sized MgZn2 precipitates and α-Mn nanoparticles, were obtained in the alloy extruded at 270 °C/0.01 mm s−1. In this alloy, the deformed coarse-grain region possessed a much stronger texture intensity (~ 32.49 mud) relative to the recrystallized fine-grain region (~ 13.99 mud). A positive work hardening rate in the third stage of work hardening curve was also evident in the alloy extruded at 270 °C, which was related to the sharp basal texture and which provided insufficient active slip systems. The high work hardening rate in the fourth stage contributed to the high ductility extruded at 270 °C/1 mm s−1. This alloy exhibited a weak texture, and the examination of fracture surface revealed highly dimpled surfaces. The optimum tensile strength was achieved in the alloy extruded at 270 °C/0.01 mm s−1, and the yield strength, ultimate tensile strength and elongation to failure were ~ 364.1 MPa, ~ 394.5 MPa and ~ 7.2%, respectively. Fine grain strengthening from the recrystallized fine-grain region played the greatest role in the strength increment of this alloy compared with Orowan strengthening and dislocation strengthening in the deformed coarse-grain regions.

Microstructures and Mechanical Properties of As-Cast and As-Extruded Mg-4.50zn-1.13ca (wt%) Alloys

Microstructure and Mechanical Properties of Mg–4.0Zn–0.5Ca Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructures and Mechanical Properties of Hot-extruded Mg-6Zn-xCu-0.6Zr(x=0,0.5,1.0,1.5) Alloys

Microstructure and Mechanical Properties of Extruded Mg–1Ca–1Zn–0.6Zr Alloy

Microstructure and Mechanical Properties of As-extruded and Heat-treated Mg-6Zn-1Mn-2Sn-0.5Ca

Microstructure and Mechanical Properties of Extruded Mg-Zn-Ca Alloy

Mechanical Properties and Microstructure of As-Cast and Extruded Mg-(Ce, Nd)-Zn-Zr Alloys

Microstructure and Mechanical Properties of As-Cast and Extruded Mg–8Li–3Al–2Zn–0.5Nd Alloy

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

Microstructure and Mechanical Properties of Extruded Mg–Zn–Mn–Ca Alloys

Microstructures and mechanical properties of Mg-Zn-Al wrought magnesium alloys

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

Microstructures and mechanical properties of as-extruded Mg–5Sn–1Zn–xAl (x=1, 3 and 5) alloys

Microstructure and Mechanical Properties of a New Hot Extruded Mg-2Ca-5Zn Alloy

High Strength Extruded Mg–5Zn–2Nd–1.5Y–0.6Zr–0.4Ca Alloy Produced by Electromagnetic Casting

Microstructure and Mechanical Properties of Mg–Zn–Ca–Ce Alloy Processed by Semi-Continuous Casting

Ultrahigh Strength Mg-Al-Ca-Mn Extrusion Alloys with Various Aluminum Contents

Microstructure and mechanical properties of as-cast and extruded Mg-8Li-1Al-0.5Sn alloy

Microstructure, Tensile Properties and Work Hardening Behavior of an Extruded Mg–Zn–Ca–Mn Magnesium Alloy

The Microstructure, Texture and Mechanical Properties of Extruded Mg–5.3Zn–0.2Ca–0.5Ce (wt%) Alloy