Abstract:A new Mg-2.2 wt% Zn alloy containing 1.8 wt% Ca and 0.5 wt% Mn has been developed and subjected to extrusion under different extrusion parameters. The finest (~ 0.48 μm) recrystallized grain structures, containing both nano-sized MgZn2 precipitates and α-Mn nanoparticles, were obtained in the alloy extruded at 270 °C/0.01 mm s−1. In this alloy, the deformed coarse-grain region possessed a much stronger texture intensity (~ 32.49 mud) relative to the recrystallized fine-grain region (~ 13.99 mud). A positive work hardening rate in the third stage of work hardening curve was also evident in the alloy extruded at 270 °C, which was related to the sharp basal texture and which provided insufficient active slip systems. The high work hardening rate in the fourth stage contributed to the high ductility extruded at 270 °C/1 mm s−1. This alloy exhibited a weak texture, and the examination of fracture surface revealed highly dimpled surfaces. The optimum tensile strength was achieved in the alloy extruded at 270 °C/0.01 mm s−1, and the yield strength, ultimate tensile strength and elongation to failure were ~ 364.1 MPa, ~ 394.5 MPa and ~ 7.2%, respectively. Fine grain strengthening from the recrystallized fine-grain region played the greatest role in the strength increment of this alloy compared with Orowan strengthening and dislocation strengthening in the deformed coarse-grain regions.

Microstructure and Mechanical Properties of As-extruded and Heat-treated Mg-6Zn-1Mn-2Sn-0.5Ca

Microstructure modification and precipitation strengthening for Mg–6Zn–1Mn–4Sn–0.5Ca through extrusion and aging treatment

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructure and Mechanical Properties of a New Hot Extruded Mg-2Ca-5Zn Alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Microstructures and Mechanical Properties of As-Cast and As-Extruded Mg-4.50zn-1.13ca (wt%) Alloys

Microstructure and Mechanical Properties of Mg–4.0Zn–0.5Ca Alloy

Study on Microstructure and Tensile Mechanical Properties of As-Extruded Mg-xZn-2.8Nd-0.6Zr-0.6Cd Alloy

Microstructure and Mechanical Properties of Extruded Mg–Zn–Mn–Ca Alloys

Microstructure, Tensile Properties and Work Hardening Behavior of an Extruded Mg–Zn–Ca–Mn Magnesium Alloy

Microstructure and mechanical properties synergistically enhanced via heat treatment modification of the as-extruded Mg-1.5Al-0.5Zn-0.2Y-0.2Ca alloy

Microstructure and mechanical properties of Mg–4Al–4Nd–0.5Zn–0.3Mn alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloy

Microstructures and Mechanical Properties of Hot-extruded Mg-6Zn-xCu-0.6Zr(x=0,0.5,1.0,1.5) Alloys

Microstructure and Tensile Properties of the Mg-6Zn-4Al-xSn Die Cast Magnesium Alloy

Microstructure and properties of Mg-9Gd-4Y-1Zn-0.5Zr alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Ca Alloy

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

Microstructure and mechanical properties of Mg-12Gd-5Y-1Sm-0.5Zr alloy

Investigation on microstructures and mechanical properties of Mg–6Zn–0.5Ce–xMn (x = 0 and 1) wrought magnesium alloys