Abstract:In this paper, mechanical properties and microstructures of the cast and extruded Al-xCu-1Li-0.4Mg–1Zn-0.1Zr alloys (x = 2.0, 3.0, 4.0, 4.5, 5.5, 6.5 wt%) were investigated. The results showed that the as-cast micrographs of alloys with different Cu content primarily consist of dendritic α-Al grains, and the intermetallic phases at the grain boundaries were Cu and Zr rich phases. After solution treatment, no recrystallization took place in extruded alloys, and the alloys mainly represented mixed textures composed of <111> and <100> fibers. Cu significantly affected the precipitation behavior of the extruded alloys. Only T1 (Al2CuLi) phases were observed in T6 (aging at 175 °C for 32 h) and T8 (3% pre-strain followed by aging at 150 °C for 32 h) treated alloy with 2 wt% Cu. Further increasing Cu contents (4.5 and 6.5 wt%) enabled the co-precipitation of T1 and θ' (Al2Cu) phases, as well as increased their density. In addition, the microstructures of grain boundaries of alloys with different Cu content showed dramatic differences. T1 phases precipitated at the grain boundaries of alloy containing 2 wt% Cu, while rare precipitation of T1 phases was observed at the grain boundaries of alloy with 6.5 wt% Cu. The yield strength (YS) of the alloys increased with the Cu content and the elongation (EL) showed an opposite trend. A good combination of ultra-high strength (YS = 684 MPa, ultimate tensile strength = 726 MPa) and ductility (EL = 6.3%) was obtained in T8 treated alloy containing 4.5 wt% Cu. The presence of the undesired coarse T2 (Al6CuLi3) phases at the grain boundaries resulted in the premature failure of the high Cu content alloys.

Microstructures and Mechanical Properties of Hot-extruded Mg-6Zn-xCu-0.6Zr(x=0,0.5,1.0,1.5) Alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructures and mechanical properties of as-extruded Mg–5Sn–1Zn–xAl (x=1, 3 and 5) alloys

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Microstructures and Mechanical Properties of As-Cast and As-Extruded Mg-4.50zn-1.13ca (wt%) Alloys

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

Microstructure and Mechanical Properties of Extruded Zn-Cu-Ti alloys

The Microstructures and Mechanical Properties of Ultrafine-Grained Mg–Zn–Zr Alloys Fabricated by Powder Metallurgy

Microstructure and Mechanical Properties of Al–6Zn–2.5Mg–1.8Cu Alloy Prepared by Squeeze Casting and Solid Hot Extrusion

Microstructure and Mechanical Properties of As-Cast and Extruded Mg–8Li–3Al–2Zn–0.5Nd Alloy

Ultra-high strength Al-Zn-Mg-Cu alloys with high zinc content prepared via powder hot extrusion

Role of Cu on the Mechanical Properties and Microstructures Evolution of Al-xCu-1Li-0.4Mg–1Zn-0.1Zr Alloys

Microstructures and mechanical properties of Mg-Zn-Al wrought magnesium alloys

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

Microstructure and Mechanical Properties of Extruded Mg–Zn–Mn–Ca Alloys

Microstructure And Mechanical Properties Of Duplex Structured Mg-Li-Zn-Y Alloys

Effect of Cu on Microstructure, Mechanical Properties, and Texture Evolution of ZK60 Alloy Fabricated by Hot Extrusion−shearing Process

Evolution of Microstructures, Texture, Damping and Mechanical Properties of Hot Extruded Mg-Nd-Zn-Zr Alloy

Microstructures and Mechanical Properties of Mg-2Y-xZn (x=1, 2, 3 At%) Alloys

Microstructures and Mechanical Properties of Ultralight Cast Al-3Li-XMg-0.1Zr Alloys

Microstructure, Texture, and Mechanical Properties of As-Extruded Mg-xLi-3Al-2Zn-0.2Zr Alloys (x = 5, 7, 8, 9, 11 Wt%)