Revealing the influence of Zr micro-alloying and hot extrusion on a novel high ductility Zn–1Mg alloy

Rui Zhao,Qiangqiang Ma,Longlong Zhang,Jiaxin Zhang,Chunxiang Xu,Yuan Wu,Jinshan Zhang

DOI: https://doi.org/10.1016/j.msea.2020.140395

2021-01-01

Abstract:<p>In this work, a novel high ductility Zn-1Mg alloy was fabricated by Zr (zirconium) micro-alloying followed by hot extrusion. The results revealed that the addition of Zr could refine the microstructure and induce the formation of Zn₂₂Zr phase in as-cast Zn-1Mg alloy. Moreover, the as-extruded Zn-1Mg-0.5Zr alloy was composed of a typical bimodal microstructure, the Zn₂₂Zr phase can effectively stimulate the dynamic recrystallization (DRX) behavior via particle-stimulated nucleation (PSN) mechanism and promote multiple slip during hot extrusion process. At the same time, compared with the as-extruded Zn-1Mg alloy, the as-extruded Zn-1Mg-0.5Zr alloy exhibited a more satisfactory combination of strength and ductility, the ultimate tensile strength (UTS) increased from 215 MPa to 260 MPa and the elongation dramatically increased from 18.5% to 36.5%. The strengthening-toughening mechanisms were systematically analysed in this work.</p>

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering