Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

A novel die-casting Mg alloy with superior performance: Study of microstructure and mechanical behavior

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Microstructure and mechanical properties of Mg-Gd-Y-Zn-Zr alloy prepared by rheo-diecasting

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Microstructure evolution and mechanical properties of an ultra-high strength casting Mg–15.6Gd–1.8Ag–0.4Zr alloy

Microstructure and Super High Strength of Cast Mg-8.5gd-2.3y-1.8ag-0.4zr Alloy

Microstructure, generation of intermetallic compounds and mechanical strengthening mechanism of as-cast Mg–4Y–xZn alloys

Microstructure and mechanical properties of Mg–4Al–4Nd–0.5Zn–0.3Mn alloy

High Performance Mg Alloy with Designed Microstructure and Phases

The Partial Substitution of Y with Gd on Microstructures and Mechanical Properties of As-Cast and As-Extruded Mg-10Zn-6Y-0.5Zr Alloy

Microstructure and Strengthening Mechanism of High Strength Mg–10Gd–2Y–0.5Zr Alloy

Microstructure, mechanical properties and fracture behaviors of large-scale sand-cast Mg-3Y-2Gd-1Nd-0.4Zr alloy

Development of a new magnesium alloy ZW21

Microstructure and Mechanical Properties of As-Cast and Extruded Mg–8Li–3Al–2Zn–0.5Nd Alloy

High Strength Extruded Mg–5Zn–2Nd–1.5Y–0.6Zr–0.4Ca Alloy Produced by Electromagnetic Casting

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

Microstructure and mechanical properties of as-cast ultralight and high strength Mg-10Li-3Al-3Zn-xY alloy with multi-precipitates

Microstructure, Tensile Properties and Work Hardening Behavior of an Extruded Mg–Zn–Ca–Mn Magnesium Alloy

Microstructures and Mechanical Properties of an Ultrathin Wall High-Pressure Die Casting Mg-8Zn-8Al (wt%) Alloy

Effects of Minor Y Addition on Microstructure and Mechanical Properties of Mg-Nd-Zn-Zr Alloy