Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Microstructure Characterization and Mechanical Properties of a Zn and Rare Earth Modified Mg Alloy

Influence of Heat Treatment and Hot Extrusion on the Microstructure and Tensile Properties of Rare Earth Modified Mg-Zn Based Alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Effect of Nd and Y Addition on Microstructure and Mechanical Properties of Extruded Mg-Zn-Zr Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Hot Extrusion Effect on the Microstructure and Mechanical Properties of a Mg–Y–Nd–Zr Alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Microstructural Evolution and Mechanical Properties of Mg-5y-5gd-Xnd-0.5zr Magnesium Alloys at Different States

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Numerical and Experimental Investigation on Hot Backward Extrusion Process of Mg-Gd-Y-Zn-Zr Magnesium Alloy

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-1Zn-0.5Zr Alloy

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

Microstructural Characteristics and Mechanical Properties of the Hot Extruded Mg-Zn-Y-Nd Alloys

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Optimization of Microstructure and Mechanical Property of a Mg-Zn-Y-Nd Alloy by Extrusion Process

High Strength Extruded Mg–5Zn–2Nd–1.5Y–0.6Zr–0.4Ca Alloy Produced by Electromagnetic Casting

Microstructure and mechanical properties synergistically enhanced via heat treatment modification of the as-extruded Mg-1.5Al-0.5Zn-0.2Y-0.2Ca alloy

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

The Research of Microstructure and Mechanical Properties of Mg–7Gd–3Y–1Nd–0.5Zn–0.5Zr (wt%) Alloy

High Performance Mg Alloy with Designed Microstructure and Phases

Influence of Multi-Pass Hot Extrusion on Microstructure and Mechanical Properties of the Mg–4Zn–1.2Y–0.8Nd Alloy