Study on Microstructure and Tensile Mechanical Properties of As-Extruded Mg-xZn-2.8Nd-0.6Zr-0.6Cd Alloy

WANG Song-tao,YANG Ping-wang,LIU Hui-hong,LIU Chu-ming
2012-01-01
Journal of Central South University
Abstract:To investigate the effect of Zn on microstructures,tensile mechanical properties of extruded Mg-xZn2.8Nd-0.6Zr-0.6Cd alloy,the optical microscope(OM),scanning electron microscope(SEM),transmission electron microscope(TEM) and universal tensile test machine were introduced.The mechanical properties of alloys with different Zn contents were compared and discussed.The results show that the grain size decreases as the content of Zn increases,followed with a bimodal grain microstructure,and the tensile strength is increased in general.The yield strength of alloy B is higher than that of alloy C because of the change of atomic ratio of Zn/Nd.The ratio of Zn/Nd in alloy B is 1.2 and the nominal ratio is 3.10,but it is 3.03 and 4.11 in alloy C respectively,which causes the number of β1′ phase precipitation in alloy B to be more than that in alloy C.Alloy D shows the highest yield strength and ultimate tensile strength,which are 340 MPa and 363 MPa,respectively,and the elongation is kept up to 9%.
What problem does this paper attempt to address?