Effect of composition on the microstructure and mechanical properties of Mg-Al-Zn alloys

Songmao Liang,Yuequn Ma,Rongshi Chen,Énhou Han
2008-01-01
Abstract:For exploiting tensile property advantage of low-cost Mg-Al-Zn casting magnesium based alloys with high strength and high ductility, the as-cast microstructure and mechanical properties of permanent-mould cast Mg-Al-Zn alloys with medium aluminum and zinc contents were investigated. SEM/EDAX and XRD analysis were carried out for microstructure observation and phase identification. By studying cooling curves acquired by thermal analysis, the solidification behavior and the temperatures of phase formation were also determined. Combined with the Mg-Al-Zn ternary phase diagram, the evolution rules of secondary phase type with Zn/Al mass ratio changing were discovered. Under this region, secondary phase varied from gamma phase to phase, T phase and quasi-crystalline phase (1 phase) with the Zn/Al mass ratio increasing. Mechanical property testing indicated that the aluminum and/or zinc content increasing, the Y.T.S (Yield Tensile Strength) increased and ductility decreased, while the U.T.S. (Ultimate Tensile Strength) firstly increased and then decreased with the peak at total element contents of 10wt.%. Both the U.T.S. and elongation of the alloy of optimum composition are superior to those of AZ91 alloy prepared at the same condition.
What problem does this paper attempt to address?