Abstract:The preparation and characteristics of silicon nanoarrays is now an attractive areas of research. At present,most research focused on the optical and electrical properties and applications,and less field emission characteristics,as a mature technology of silicon planar support, silicon field emission cathode materials are easily compatible with the microelectronic integrated circuits, and so they have a broad application prospects.We present the fabrication of large-scale two dimensional periodic silicon nanoarrays using nanosphere lithography,and the field emission characteristics have been studied. The fabrication process includes following steps: first the crystalline silicon substrate was coated with a monolayer of self polystyrene (PS) spheres of 220 nm in diameter, then the sample was etched by reactive ion etching to produce silicon nanoarrays. AFM images of the nanoarrays show that the tips stand 60～70 nm high and the area density can achieve 6×109/cm2. All field emission measurements were performed at a vacuum of 1.0×10-4 Pa or better. Expected to improve the field emission characteristics, about 60 nm thickness of a amorphous carbon film was deposited on top of the silicon nanoarrays by plasma-enhanced chemical vapour deposition. Field emission results show that compared to silicon nanoarrays, silicon nanoarrays coated with a thin a-C film effectively lower the threshold fields, approximately 8.1 V/μm, while field enhancement factor increased. When the electric field intensity reached 20 V/μm, the current density can reach about 1.4 mA/cm2. The improvement of field emission originates from the anisotropic structure of the films,when conductive sp2 clusters embedded in an insulating sp3 matrix,the electric field has been enhanced.

Controlling Growth And Field Emission Properties Of Silicon Nanotube Arrays By Multistep Template Replication And Chemical Vapor Deposition

Controlling the growth and field emission properties of silicide nanowire arrays by direct silicification of Ni foil.

Field Emission Properties of Carbon Nanotubes Grown on Silicon Nanowire Arrays

Large-Scale Aligned Silicon Carbonitride Nanotube Arrays: Synthesis, Characterization, and Field Emission Property

Hot electron field emission via individually transistor-ballasted carbon nanotube arrays.

Controlling Growth and Field Emission Property of Aligned Carbon Nanotubes on Porous Silicon Substrates

Electron Field Emission Characteristics from Single-crystal Silicon Nanoarrays Fabricated by Direct Lithography with Nanosphere Mask

OS1503 Development of Highly Ordered Silicon Nanowire Array

Formation and Field Emission Characteristics of Amorphous and Crystalline Si Nanoarrays

An Ordered Si Nanowire with NiSi2 Tip Arrays As Excellent Field Emitters.

Field Electron Emission From Individual Carbon Nanotubes Of A Vertically Aligned Array

Fabrication and Field Emission Properties of Multi-Walled Carbon Nanotube/silicon Nanowire Array

Morphology Control and Electron Field Emission Properties of High-Ordered Si Nanoarrays Fabricated by Modified Nanosphere Lithography

Fabrication of Vertically Aligned Si Nanowires and Their Application in A Gated Field Emission Device

Enhanced Field Emission From Imprinted Carbon Nanotube Arrays

Self-Oriented Regular Arrays of Carbon Nanotubes and Their Field Emission Properties

Controlling Growth of Aligned Carbon Nanotubes from Porous Silicon Templates

FORMATION AND FIELD EMISSION CHARACTERISTICS OF AMORPHOUS AND CRYSTALLINE <font>Si</font> NANOARRAYS

A Novel Controllable Synthesis of Silica Nanotube Arrays with Ultraviolet Photoluminescence

Aligned SiC Porous Nanowire Arrays with Excellent Field Emission Properties Converted from Si Nanowires on Silicon Wafer

Fabrication and field emission property of a Si nanotip array