Abstract:We report the nanocluster-catalyzed growth of ultralong and highly uniform single-crystalline silicon nanowires (SiNWs) with millimeter-scale lengths and aspect ratios up to approximately 100,000. The average SiNW growth rate using disilane (Si 2H 6) at 400 degrees C was 31 microm/min, while the growth rate determined for silane (SiH 4) reactant under similar growth conditions was 130 times lower. Transmission electron microscopy studies of millimeter-long SiNWs with diameters of 20-80 nm show that the nanowires grow preferentially along the 110 direction independent of diameter. In addition, ultralong SiNWs were used as building blocks to fabricate one-dimensional arrays of field-effect transistors (FETs) consisting of approximately 100 independent devices per nanowire. Significantly, electrical transport measurements demonstrated that the millimeter-long SiNWs had uniform electrical properties along the entire length of wires, and each device can behave as a reliable FET with an on-state current, threshold voltage, and transconductance values (average +/-1 standard deviation) of 1.8 +/- 0.3 microA, 6.0 +/- 1.1 V, 210 +/- 60 nS, respectively. Electronically uniform millimeter-long SiNWs were also functionalized with monoclonal antibody receptors and used to demonstrate multiplexed detection of cancer marker proteins with a single nanowire. The synthesis of structurally and electronically uniform ultralong SiNWs may open up new opportunities for integrated nanoelectronics and could serve as unique building blocks linking integrated structures from the nanometer through millimeter length scales.

An Ordered Si Nanowire with NiSi2 Tip Arrays As Excellent Field Emitters.

Controlling the growth and field emission properties of silicide nanowire arrays by direct silicification of Ni foil.

Well-Aligned Nisi/Si Heterostructured Nanowire Arrays As Field Emitters

Array-orderly single crystalline silicon nano-wires

OS1503 Development of Highly Ordered Silicon Nanowire Array

Tunable field emission properties of well-aligned silicon nanowires with controlled aspect ratio and proximity

A Novel Sulfide-Assisted Growth of Silicon Nano-Wires

Direct Growth of Ni2Si Nanowire Array Electrodes for High-performance Reversible Lithium-ion Batteries

Ordered Arrays of High-Quality Single-Crystalline Α-Si3n4 Nanowires: Synthesis, Properties and Applications

Aligned SiC Porous Nanowire Arrays with Excellent Field Emission Properties Converted from Si Nanowires on Silicon Wafer

Preparation, superior field emission properties and first principles calculation of electronic structure of SiC nanowire arrays on Si substrate

Controlled-Direction Growth of Planar InAsSb Nanowires on Si Substrates Without Foreign Catalysts

Controlling Growth And Field Emission Properties Of Silicon Nanotube Arrays By Multistep Template Replication And Chemical Vapor Deposition

Field emission of comb-like chromium disilicide nanowires prepared by an in situ chloride-generated route

Terrace-confined guided growth of high-density ultrathin silicon nanowire array for large area electronics

Solid-State Limited Nucleation of NiSi/SiC Core-Shell Nanowires by Hot-Wire Chemical Vapor Deposition

Growth of Nickel Films on the Surface of Silicon Nanowire

Fabrication and Field Emission Properties of Multi-Walled Carbon Nanotube/silicon Nanowire Array

Silicon Nanowires, Catalytic Growth and Electrical Characterization

Self-Assembled Zns Nanowire Arrays: Synthesis, in Situ Cu Doping and Field Emission

Controlled synthesis of millimeter-long silicon nanowires with uniform electronic properties.