Abstract:The quasi-static consolidation in uniaxial compression of combustion synthesized TiB2–Cu composite with 40 wt.% Cu from Ti, B and Cu powders was investigated. Thermodynamics of the system was calculated theoretically. It was found that TiB2 was a stable phase in the composite and TiCu interphase compound can convert into stable phase. The phases of the synthesized product were identified using X-ray diffraction and the results showed only TiB2 and Cu phases, no other phases existed in the product. It is consistent with the calculated result of thermodynamics. The consolidated product was dense and no apparent pores existed in the microstructure. Fine TiB2 reinforcement grows in near equivalent axis-like and block-like shapes. As a binder phase, copper metal was found between TiB2 and TiB2 particles. It is shown that copper improves the densification behavior during combustion synthesis, compared with synthesized pure TiB2 ceramic. Due to the addition of copper, the relative density, bend strength and fracture toughness of TiB2–Cu composite are much higher than those of TiB2 ceramic. Crack-tip plastic blunting by a ductile metallic phase and crack deflection by the stress due to the difference of thermal expansion coefficient and elastic modulus between TiB2 and Cu are the principal mechanisms of toughness improvement of TiB2–Cu composite.

Large-scale (Ti,Cr)B2-Cu composite by combustion synthesis

Large-Scale (Ti,cr)b2-Cu Composite by Combustion Synthesis

Large-Scale (Ti,Cr)B<sub>2</sub>-Cu Composite by Combustion Synthesis

Combustion Synthesis and Densification of Titanium Diboride–copper Matrix Composite

In Situ Combustion Synthesis of TiB<sub>2</sub>-AIN Composites

Self-propagating high-temperature synthesis of TiC-TiB2/Cu ceramic-matrix composite

Preparation of Tib2 Nanoparticles Reinforced Cu-Matrix Composite by Direct Combustion Synthesis

Combustion Synthesis and Two-Time Densification of TiB<sub>2</sub>-Cu Composites

Large-Scale Solidified Tib2-(Ti,W)C Composite Ceramics Prepared By Combustion Synthesis Under High Gravity

Self-propagating high temperature combustion synthesis of TiC/TiB2 ceramic–matrix composites

B4C‒TiB2 composite with modified microstructure and enhanced properties from optimal size coupling of raw powders

Combustion Synthesis and Two-Time Densification of TiB2-Cu Composites

The Process of TiB 2 −cu Composite Phase and Structure Formation During Combustion Synthesis

Combustion Synthesis of Ti(C,N)-TiB_2 Composite Powders under Super Gravity Conditions

Self-Propagating High-Temperature Synthesis, Microstructure and Mechanical Properties of Tic-Tib2-Cu Composites

Self-propagating high temperature combustion synthesis of TiB/Ti composites

Combustion synthesis of Ti(C, N) TiB2 composite powders under super gravity conditions

Preparation and Properties of Solidified TiC-TiB2 with Hypoeutectic, Eutectic and Hypereutectic Microstructures

The influences of cu content on the self-propagating high temperature synthesized TiC-TiB2 composites

Microstructure Transformation and Mechanical Properties of TiC–TiB2 Ceramics Prepared by Combustion Synthesis in High Gravity Field

Combustion synthesis and densification of large-scale TiC–xNi cermets