Abstract:The as-cast Ti1.02Cr1.1Mn0.3Fe0.6 alloy for hybrid hydrogen storage vessel application was annealed at different temperatures (873 K, 973 K, 1123 K, 1173 K) for 2 h, and annealed at 1123 K for different time (2, 5, 8 h) respectively, and their microstructure and hydrogen storage properties were investigated systematically. The results show that the as-cast alloy has a single C14 Laves phase, and all annealed alloys consist of a C14 Laves main phase and a secondary phase. After annealing at different temperatures for 2 h, the hydrogen absorption pressure at 298 K decreases, however, the maximum hydrogen storage capacity and desorption pressures at 318 K decrease slightly too. As the annealing time extends, the hydrogen absorption plateau pressure at 298 K and hydrogen desorption plateau pressure at 318 K increase, and the hydrogen desorption capacity increases first and then decreases, which reaches the highest desorption capacity of 1.721 wt.% at the annealing time of 5 h. Among the studied alloys, the alloy annealed at 1123 K for 5 h has the best overall properties for hybrid hydrogen storage application, its hydrogen absorption plateau at 298 K is 29.09 MPa, its hydrogen desorption plateau pressure at 318 K is 45.12 MPa, its hydrogen storage capacity is 1.721 wt.% and its dissociation enthalpy (Delta H-d) is 17.78 kJ/mol H-2. (C) 2015 Elsevier B.V. All rights reserved.

Effect of Surface Oxide Layer on the Activation Behavior of Timn1.25cr0.25 Hydrogen Storage Alloy

Effect of Surface Oxide Layer on Activation Performance of Hydrogen Storage Alloy TiMn1.25Cr0.25

Activation performance of TiMn1.25Cr0.25 hydrogen storage alloy with various particle sizes

Effect of V Addition on Activation Performances of TiMn1.25Cr0.25 Hydrogen Storage Alloy

Activation and Hydrogen Absorption-Desorption Properties of Timn0.85cr0.35v0.3 Alloy

Surface Characterization of Thermally Oxidized Titanium Alloys

Effect of Carbon Addition on Activation and Hydrogen Sorption Characteristics of TiMn1.25Cr0.25 Alloy

The activation mechanism of Ti–V-based hydrogen storage alloys

Effect of Carbon on Hydrogen Storage Performances of TiMn1.25Cr0.25 Alloy

Influence of Annealing Treatment on the Microstructure and Hydrogen Storage Performance of Ti1.02Cr1.1Mn0.3Fe0.6 Alloy for Hybrid Hydrogen Storage Application

The Effect of Cr Content on the Structural and Hydrogen Storage Characteristics of Ti10V80−xFe6Zr4Crx (x = 0–14) Alloys

The Effects of Partial Substitution of Mn by Cr on the Phase Structure, Microstructure and Electrochemical Properties of Ti-Zr-V-Mn-Ni Hydrogen Storage Alloys

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Effect of Mn Substitution for Co on the Structural, Kinetic, and Thermodynamic Characteristics of ZrCo1−Mn (x=0–0.1) Alloys for Tritium Storage

Phase Structures and Hydrogen Storage Properties of TiV1.35Cr1.35-xMnx Alloys(x=0～0.45)

Influence of the Substitution Cr for Mn on Structural and Hydrogen Storage Performance of Ti 0.9 Zr 0.1 V 0.45 Cr X Mn 1.5-X (x=0, 0.05, 0.1, 0.15, 0.2) Alloys

Microstructure and hydrogen storage properties of Ti1.0VxMn2-x(x=0.6 similar to 1.6) alloys

Microstructure and hydrogen storage properties of Ti1.0VxMn2-x(x=0.6-1.6) alloys

Effect of Cr Content on the Sorption Performance of Timn1.2-Xcrxv0.25fe0.05

The Effect of Tungsten Additive on the Surface Characteristics of Amorphous Ni–P Alloy

Effect of Annealing on Phase Structure and Performance of TiMn-based Hydrogen Storage Alloy