Abstract:The microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x = 0, 5, 10, 15) alloys have been studied. XRD and SEM analyses show that all alloys consist of a BCC main phase and a small fraction of C14 Laves secondary phase, in which the latter precipitates along the grain boundary of the former becoming network structure. With increasing Ti content in the alloy, the lattice parameter and cell volume of the BCC main phase of the alloy increase. The chemical composition of each phase is analysed by EDS, from which the lattice parameters of BCC phase have a good linear relationship with their average atomic radii. All bulk alloys have good activation behaviors and hydriding kinetics. With the increase of Ti content, the incubation time for activation decreases first and then increases under an initial hydrogen pressure of 4 MPa at 298 K. The incubation time of Ti15V75Fe6Zr4 alloy is only 12 s. It is one of the shortest incubation time in V-based solid solution alloys as far as we know, which may be related to the existence of C14 Laves phase. All the alloys have relatively high hydrogen absorption capacities of above 3 wt%, which increase first and then decrease as the Ti content increases, achieving the maximum capacity of 3.61 wt% at x = 10 at 298 K. With increasing x, the equilibrium plateau pressure of dehydrogenation of the samples at 353 K decreases owing to the expansion of unit cell of main phase, which is far below 0.1 MPa for x = 10 and 15. The maximum desorption capacity of 1.94 wt% (desorbed to 0.001 MPa) is obtained at x = 5, compared to that of 1.6 wt% (desorbed to 0.1 MPa) achieved at x = 0.

The activation mechanism of Ti–V-based hydrogen storage alloys

Effect of V Addition on Activation Performances of TiMn1.25Cr0.25 Hydrogen Storage Alloy

Improvement of Activation Performance of the Quenched Ti–V-based BCC Phase Alloys

Activation performance of TiMn1.25Cr0.25 hydrogen storage alloy with various particle sizes

Hydrogen storage performance of quenched Ti–V-based alloy

Activation and Hydrogen Absorption-Desorption Properties of Timn0.85cr0.35v0.3 Alloy

Effect of Surface Oxide Layer on Activation Performance of Hydrogen Storage Alloy TiMn1.25Cr0.25

Effects of Melt-Quenching Rates on the Hydrogen Storage Properties of Ti-based BCC Phase Alloy

Hydrogen storage properties of V+TiFe0.85Mn0.15 multi-phase alloys

Hydrogen storage capabilities of the alloys Fe 0.85Mn 0.15Ti 0.9M 0.1 (M=Zr, V, Ca)

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Influence of Heat Treatment on the Microstructure and Hydrogen Storage Properties of Ti10V77Cr6Fe6Zr Alloy

Effect of Rapid Quenching on Phase Structure and Hydrogen Storage Performance of Ti-V-Based Bcc Phase Alloys

The Effect of Cr Content on the Structural and Hydrogen Storage Characteristics of Ti10V80−xFe6Zr4Crx (x = 0–14) Alloys

Improvements of Activation Performance for Hydrogen Storage Alloys

Microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x=0~15) alloys

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys

Effect of Surface Oxide Layer on the Activation Behavior of Timn1.25cr0.25 Hydrogen Storage Alloy

Studies of hydrogen storage properties and absorption-desorption mechanism of FeTi1.3(Mm)y alloy

Microstructure and hydrogen storage properties of Ti1.0VxMn2-x(x=0.6-1.6) alloys

Microstructure and hydrogen storage properties of Ti10V84-xFe6Zrx (x = 1-8) alloys