Abstract:In order to improve the activation behavior of Ti1.02Cr1.1Mn0.3Fe0.6 alloy with high hydrogen desorption pressure for hybrid hydrogen storage vessel application, the rare earth (RE) doped Ti1.02Cr1.1Mn0.3Fe0.6RE0.03 (RE = La, Ce, Ho) alloys were prepared by induction levitation melting. The effect of rare earth doping on the microstructures and hydrogen storage properties was also investigated systematically. The results show that Ti1.02Cr1.1Mn0.3Fe0.6 alloy displays a single C14 Laves phase, and there is a secondary phase of rare earth oxide in the RE doped alloys. The RE doping strategy can expand the unit cell volume of C14 Laves main phase. After RE doping, the activation behavior of the Ti1.02Cr1.1Mn0.3Fe0.6RE0.03 alloy is obviously improved and the hydrogen storage capacity is increased, while the hydrogen desorption plateau pressure is decreased. Moreover, the RE-free alloy can hardly absorb hydrogen at room temperature under 34-43 MPa hydrogen pressure, but all RE-doped alloys can absorb hydrogen to saturation under the same condition. The decline of pressure plateau is inversely proportional to the atomic number of RE. Among the studied alloys, the Ti(1.02)Cr(1.1)Mn(0.3)Fe(0.6)La0.03 alloy shows the best overall properties and can be fully activated at room temperature. Its hydrogen absorption pressure is 39.31 MPa and 51.27 MPa under 298 K and 318 K, respectively. Its hydrogen storage capacity is up to 1.715 wt% and the dissociation enthalpy is 16.63 kJ/mol H-2 with a desorption plateau slope of 0.098. (C) 2017 Published by Elsevier B.V.

Activation and Hydrogen Absorption-Desorption Properties of Timn0.85cr0.35v0.3 Alloy

Effect of V Addition on Activation Performances of TiMn1.25Cr0.25 Hydrogen Storage Alloy

Effect of Rare Earth Doping on the Hydrogen Storage Performance of Ti1.02Cr1.1Mn0.3Fe0.6 Alloy for Hybrid Hydrogen Storage Application

Experimental and Theoretical Investigation on the Enhanced Hydrogen Storage Performance of Ti–Cr–Mn–Fe-Based Alloys Modified by Nb Substitution

Effect of Surface Oxide Layer on Activation Performance of Hydrogen Storage Alloy TiMn1.25Cr0.25

Phase Structures and Hydrogen Storage Properties of TiV1.35Cr1.35-xMnx Alloys(x=0～0.45)

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys

Influence of Annealing Treatment on the Microstructure and Hydrogen Storage Performance of Ti1.02Cr1.1Mn0.3Fe0.6 Alloy for Hybrid Hydrogen Storage Application

Phase structures and hydrogen storage properties

Effect of Carbon Addition on Activation and Hydrogen Sorption Characteristics of TiMn1.25Cr0.25 Alloy

Hydrogen Storage Characteristics of TiMn1.25-5yCr0.25(V4Fe)y Alloys

Effect of Surface Oxide Layer on the Activation Behavior of Timn1.25cr0.25 Hydrogen Storage Alloy

Hydrogen storage capabilities of the alloys Fe 0.85Mn 0.15Ti 0.9M 0.1 (M=Zr, V, Ca)

Hydrogen storage properties of V+TiFe0.85Mn0.15 multi-phase alloys

Activation performance of TiMn1.25Cr0.25 hydrogen storage alloy with various particle sizes

Hydrogen Storage Properties and Crystal Structure of Ti-Cr Based Alloys

Studies of hydrogen storage properties and absorption-desorption mechanism of FeTi1.3(Mm)y alloy

Hydrogen storage properties of TiMn2-based alloys

Effect of Carbon on Hydrogen Storage Performances of TiMn1.25Cr0.25 Alloy

Influence of the Substitution Cr for Mn on Structural and Hydrogen Storage Performance of Ti 0.9 Zr 0.1 V 0.45 Cr X Mn 1.5-X (x=0, 0.05, 0.1, 0.15, 0.2) Alloys

The activation mechanism of Ti–V-based hydrogen storage alloys