Abstract:In current work, Cu-20wt%W (Cu-20W) composite of near theoretical density (99.69 %) and high electrical conductivity (86.78 %IACS) was fabricated by spray drying technique and hot isostatic pressing (HIP), aiming to enhance the mechanical properties of Cu-W composite while maintaining high conductivity. The impacts of W nanoparticles on the microstructure and properties of Cu-20W samples were evaluated. Adding W nanoparticles can remarkably refine the grain of Cu and strengthen the Cu-W composite through a pinning effect. Room temperature tensile strength and compressive yield strength of Cu-20W composite were 380 MPa and 304.49 MPa, which are 117.14 % and 616.95 % higher than that of pure Cu (175 MPa and 42.47 MPa), respectively. Tungsten nanoparticles can promote the high-temperature reliability of Cu-W samples. Tensile strength of pure Cu and Cu-20W sample gradually decreased with increasing test temperature, but the percentage increment of tensile strength increased. The tungsten particles pinned at grain boundaries during hot deformation inhibit recrystallization grain growth and hinder dislocation movement, thereby contributing to the high-temperature properties of Cu-20W composite. The peak stress of Cu-20W sample is 146.60 % higher than pure Cu, even at close to the melting point of Cu (940 °C). The strength of Cu-20W composite is heightened by combining fine-grain strengthening and dispersion strengthening due to the introduced W nanoparticles.

Study of process of fine-grained W-Cu composites

Long-term Ball Milling and Hot Pressing of In-Situ Nanoscale Tungsten Carbides Reinforced Copper Composite and Its Characterization

Microstructural studies of W–10wt.% Cu composites prepared by using ultrafine composite powder

Effect of sintering temperature on fine-grained Cu W composites with high copper

Synthesis and Characterizations of Nanocrystalline Wc-Co Composite Powders by A Unique Ball Milling Process

Study of a New Method to Fabricate W–Cu Composites

Mechanical milling and its influence on microstructure and electric conductivity of high mass fraction TiC / Cu composites

W–Cu Composite with High W Content Prepared by Grading Rounded W Powder with Narrow Particle Size Distribution

Fabrication of Cu-riched W-Cu composites by combustion synthesis and melt-infiltration in ultrahigh-gravity field

Effect of Grain Refinement on the Comprehensive Mechanical Performance of W–Cu Composites

Nanocrystal W-Cu electrical contact material by mechanical alloying and hot pressed sintering

Preparation and Properties of Fine-Grained and Ultrafine-Grained W-TiC-Y2O3 Composite

Microstructure and Mechanical Properties of Nanocrystalline Wc-Particle-Reinforced Ti-Based Composites with Nano/Ultrafine-Grained Intermetallic Matrix from Spark Plasma Sintering and Crystallization of Amorphous Phase

Microstructure, mechanical properties and arc erosion behavior of CuW composites prepared by high energy ball milling and spark plasma sintering

Study on synthesis and structure of mechanically alloyed W-Ni-Fe nanocomposite powders

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

Ultrafine W-Cu Composite Powder Research Progress

The Influence of Mechanical Milling on the Properties of W–40wt.%Cu Composite Produced by Hot Extrusion

The influence of mechanical milling on microstructure and the properties of W-40Cu composite by hot extrusion

Preparation and properties of Al2O3 dispersed fine-grained W-Cu alloy

Effect of nano-Y2O3 on the microstructure and mechanical properties of Cu-10W composites prepared by spark plasma sintering