EFFECTS OF Bi2 O3 ON PHASE COMPONENTS, MICROSTRUCTURE AND PROPERTIES OF THE CORDIERITE CERAMICS

陈国华,刘心宇

DOI: https://doi.org/10.3321/j.issn:0454-5648.2003.09.015

2003-01-01

Abstract:Bi2O3 is used as an additive in the sintering of cordierite ceramie in order to obtain ceramies with high amount of cordierite and to decrease the sintering temperature. The cordierite ceramies were prepared by powder sintering method. The effects of Bi2O3 on the transformation, the phase components and properties of cordierite ceramies were studied using XRD, SEM, DTA and thermal dilatometer. The function of Bi2O3 additive is to produc?liquid phase in lower temperature period in the sintering process . The results show that the sintering temperature is obviously decreased by adding Bi2O3. When sintered at 1350℃ for 3 h, the ceramies are composed of α-cordierite and isolated glass phase. The density, bending strength and the thermal expansion coefficient increase with the increasing of Bi2O3 content . The optimum content of Bi2O3 is 4% (in mass frac-tion). The decrease of the binding power of Si - O network and the existence of some glass phase are the main cause to increase the thermal expansion coefficient of the cordierite ceramies.