Influence of La3+, Ce4+ on phase transition and sintering property of cordierite material prepared by solid reaction

Xudong Luo,Dianli Qu,Zhipeng Xie

DOI: https://doi.org/10.11785/S1000-4343.20130212

2013-01-01

Abstract:The cordierite was prepared by solid reaction with raw materials including decomposed magnesite, industrial alumina and SiO2 powder with different content of lanthana, ceria as additives. The crystalline phases and microstructure were determined by XRD and SEM respectively. The lattice parameters and crystallinity of the crystalline phases were estimated by X'Pert plus software. The phase composition was evaluated by semi-quantification method, and grain size was calculated by Scherrer formula. The effect of La3+ and Ce4+ on composition, grain size, lattice parameters, crystallinity, microstructure, and sintering property of cordierite materials was studied. The results showed that the sintering property of lanthana as sintering aid for cordierite materials was better than that of ceria. The cordierite material added with lanthana was denser than with ceria as sintering aid. The lattice parameters and lattice volume of cordierite were firstly increased and then decreased with the addition of lanthana and ceria. The phase transition of cordierite, which resulted in mullite, was facilitated due to the higher ionic field intensity of Ce4+ than that of La3+.