Effect of Bi2O3 on Sintering and Dielectric Properties of Cordierite Ceramics Synthesized by Sol-Emulsion-Gel Technique

Wang Shaohong,Lu Haoran,Hou Zhaoxia,Hu Xiaodan,Niu Changlei,Xue Zhaolu,Wang Hao,Wang Cai

2011-01-01

Rare Metal Materials and Engineering

Abstract:Mg2Al4Si5O18 dielectric ceramics were prepared by sol-emulsion-gel technique. The effect of Bi2O3 addition on sintering, crystallization mechanism and dielectric properties were studied. The results indicate that cordierite could be sintered compactly at 900 degrees C for 2 h by doping 4wt% Bi2O3; the nucleation of mu-cordierite can be inhibited and mu-cordierite is crystallized directly by adding Bi2O3. The sintered sample possesses excellent dielectric properties (epsilon=3.92, tg delta=0.0012, and 1 GHz), which is qualified for low temperature co-firing with silver electrode well. So it is an ideal dielectric material for high frequency multi-layer chip inductors and other electronic components. However, overmuch addition of 5wt% Bi2O3 could make the dielectric properties of the cordierite worse.