Abstract:In current work, Cu-20wt%W (Cu-20W) composite of near theoretical density (99.69 %) and high electrical conductivity (86.78 %IACS) was fabricated by spray drying technique and hot isostatic pressing (HIP), aiming to enhance the mechanical properties of Cu-W composite while maintaining high conductivity. The impacts of W nanoparticles on the microstructure and properties of Cu-20W samples were evaluated. Adding W nanoparticles can remarkably refine the grain of Cu and strengthen the Cu-W composite through a pinning effect. Room temperature tensile strength and compressive yield strength of Cu-20W composite were 380 MPa and 304.49 MPa, which are 117.14 % and 616.95 % higher than that of pure Cu (175 MPa and 42.47 MPa), respectively. Tungsten nanoparticles can promote the high-temperature reliability of Cu-W samples. Tensile strength of pure Cu and Cu-20W sample gradually decreased with increasing test temperature, but the percentage increment of tensile strength increased. The tungsten particles pinned at grain boundaries during hot deformation inhibit recrystallization grain growth and hinder dislocation movement, thereby contributing to the high-temperature properties of Cu-20W composite. The peak stress of Cu-20W sample is 146.60 % higher than pure Cu, even at close to the melting point of Cu (940 °C). The strength of Cu-20W composite is heightened by combining fine-grain strengthening and dispersion strengthening due to the introduced W nanoparticles.

Deformation Processed Cu-15 Wt Pct Cr Composite Synthesized by Hot Hydrostatic Extrusion of Mechanical Milled Powders

Attaining Exceptional Electrical Conductivity in Cu-Fe Composite by Powder Rolling Strategy

Achieving Homogeneous Fe Distribution and High Strength in Cu-Fe Composite Consolidated by Powder Rolling

Densification of Cu-15wt%Cr composite powders prepared by mechanical milling

Structures, Properties and Responses to Heat Treatment of Deformation Processed Cu-15% Cr Composite Powders Prepared by Mechanical Milling

Tungsten Copper Composite Fabricated by Compound Plastic Deformation Technologies

Microstructure and properties of tungsten copper produced by hot deformation densification technology

Fabrication of High Strength Conductivity Submicron Crystalline Cu-5%Cr Alloy by Mechanical Alloying

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

W-Cu Composites Subjected To Heavy Hot Deformation

Research on Densification of Tungsten-Copper Powders by Sintering and Hot Hydrostatic Extrusion

Distinct Electrical and Mechanical Responses of a Cu-10Fe Composite Prepared by Hot-Pressed Sintering and Post Treatment

Effect of Iron Content on the Strength and Conductivity of Cu-Fe In Situ Composite

Microstructure and Properties of Heavily Drawn Cu-Ag-Fe Composites

Mechanical deformation and properties of CuCr25 alloy

Strain Strengthening Of Ag-10cu In Situ Filamentary Composite Prepared By Heavy Deformation

Study on hot-hydrostatic extrusion of mechanically alloyed nanocrystalline Cu-5%Cr powders

Phases Interface in Deformation Processed Cu–15 Wt.%cr Composite Prepared by Elemental Powders

Hot Deformation Behavior and Processing Maps of Diamond/Cu Composites

The Influence of Mechanical Milling on the Properties of W–40wt.%Cu Composite Produced by Hot Extrusion

A Novel Way for Fabricating Ultrafine Grained Cu-4.5 Vol% Al2O3 Composite with High Strength and Electrical Conductivity