A Novel Way for Fabricating Ultrafine Grained Cu-4.5 Vol% Al2O3 Composite with High Strength and Electrical Conductivity

Chenguang Li,Yuehuang Xie,Dengshan Zhou,Wei Zeng,Jun Wang,Jiamiao Liang,Deliang Zhang
DOI: https://doi.org/10.1016/j.matchar.2019.06.017
IF: 4.537
2019-01-01
Materials Characterization
Abstract:Ultrafine grained Cu-4.5 vol% Al2O3 bulk composite samples were fabricated by a novel way involving three steps: (i) dealloying of a Cu-50wt.%Al alloy powder to produce a nanocrystalline Cu-0.8wt.%Al-1.5wt.%O powder; (ii) heat treatment of the as-dealloyed powder using two different routes to obtain Cu-Al2O3 composite powders with Al2O3 particles distributed either at Cu grain boundaries or within Cu grains, and (iii) consolidation of the powders by powder compact extrusion. The microstructures, mechanical properties and electrical conductivity of the composite samples were investigated. The composite sample with a dispersion of intragranular Al2O3 nanoparticles exhibited an excellent combination of a high tensile strength (522 MPa), good ductility (elongation to fracture: 8.2%) and a high electrical conductivity (90%IACS). The correlation among the microstructure, mechanical properties and electrical conductivity is discussed.
What problem does this paper attempt to address?