STUDY ON THE STRUCTURE OF TiB2-ZrB2 COMPOSITES PREPARED BY HOT PRESSING

王皓,王为民,辜萍,傅正义,袁润章

DOI: https://doi.org/10.3321/j.issn:0454-5648.2002.04.016

2002-01-01

Abstract:TiB2-ZrB2 solid solution composites were prepared by hot pressing. The effects of the additive content on the phase constituent and the crystal structure of the composite were investigated by the X-ray diffraction analysis. The microstructure analysis was carried out by EPMA, SEM and TEM. Under the experimental condition, it is shown that crystal parameters increase with the increase of the ZrB2 content and reach the maximum value when the ZrB2 content is 8% (in mole). Two types of boride, Ti-rich and Zr-rich compounds, are found in the composite due to ZrB2 partly dissolving in the TiB2 matrix at the interface. The velocity of the grain boundary immigration decreases effectively by the solid solution reaction during sintering, which redounds to gain uniform grains in the composite.